Fabrication of iron-rich Fe-Al intermetallics using the wire-arc additive manufacturing process

被引：124

作者：

Shen, Chen ^{[1
]}

Pan, Zengxi ^{[1
]}

Ma, Yan ^{[1
]}

Cuiuri, Dominic ^{[1
]}

Li, Huijun ^{[1
]}

机构：

[1] Univ Wollongong, Fac Engn & Informat Sci, Northfields Ave, Wollongong, NSW 2522, Australia

来源：

ADDITIVE MANUFACTURING | 2015年 / 7卷

关键词：

Iron aluminide; In situ alloying; Additive manufacturing; GTAW; ALLOYING ADDITIONS; MICROSTRUCTURE; LASER; ALUMINIDES; DEPOSITION; COMPONENTS; TITANIUM; CREEP; STEEL;

D O I：

10.1016/j.addma.2015.06.001

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A wire-arc additive manufacturing (WAAM) system is used to fabricate iron rich Fe-Al intermetallics with 25 at% aluminum content. The alloy is produced in situ through controlled addition of the elemental iron and aluminum components into the welding process. The properties of the fabricated material are assessed using optical microstructure analysis, hardness testing, tensile testing, X-ray diffraction phase characterization and electron dispersive spectrometry. It is shown that the WAAM system is capable of producing iron rich Fe-Al intermetallics with higher yield strength and similar room temperature ductility when compared to equivalent materials produced using powder metallurgy. Crown Copyright (C) 2015 Published by Elsevier B.V. All rights reserved.

引用

页码：20 / 26

页数：7

共 31 条

[1] Enhancement of high temperature strength and room temperature ductility of iron aluminides by alloying [J].

Bahadur, A .

MATERIALS SCIENCE AND TECHNOLOGY, 2003, 19 (12) :1627-1634

[2]

Baker I., 1999, INT MATER REV, V552, P181

[3] Additive manufacturing of Ti-6Al-4V components by shaped metal deposition: Microstructure and mechanical properties [J].

Baufeld, Bernd ;

Van der Biest, Omer ;

Gault, Rosemary .

MATERIALS & DESIGN, 2010, 31 :S106-S111

[4] Additive manufactured Ti-6Al-4V using welding wire: comparison of laser and are beam deposition and evaluation with respect to aerospace material specifications [J].

Brandl, E. ;

Baufeld, B. ;

Leyens, C. ;

Gault, R. .

LASER ASSISTED NET SHAPE ENGINEERING 6, PROCEEDINGS OF THE LANE 2010, PART 2, 2010, 5 :595-606

[5] Morphology, microstructure, and hardness of titanium (Ti-6Al-4V) blocks deposited by wire-feed additive layer manufacturing (ALM) [J].

Brandl, Erhard ;

Schoberth, Achim ;

Leyens, Christoph .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 532 :295-307

[6] Modeling of pulsed GTAW based on multi-sensor fusion [J].

Chen, Bo ;

Wang, Jifeng ;

Chen, Shanben .

SENSOR REVIEW, 2009, 29 (03) :223-232

[7] Development of a direct metal freeform fabrication technique using CO2 laser welding and milling technology [J].

Choi, DS ;

Lee, SH ;

Shin, BS ;

Whang, KH ;

Song, YA ;

Park, SH ;

Jee, HS .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 113 (1-3) :273-279

[8] EFFECT OF BORON ON THE TENSILE PROPERTIES OF B2 FEAL [J].

CRIMP, MA ;

VEDULA, K .

MATERIALS SCIENCE AND ENGINEERING, 1986, 78 (02) :193-200

[9]

Dutta B, 2011, ADV MATER PROCESS, V169, P33

[10] EQUILIBRIUM-POINT DEFECTS IN INTERMETALLICS WITH THE B2 STRUCTURE - NIAL AND FEAL [J].

FU, CL ;

YE, YY ;

YOO, MH ;

HO, KM .

PHYSICAL REVIEW B, 1993, 48 (09) :6712-6715

← 1 2 3 4 →