Laterally graded multilayer double-monochromator

被引：6

作者：

Macrander, AT ^{[1
]}

Als-Nielsen, J ^{[1
]}

Liu, C ^{[1
]}

Krasnicki, S ^{[1
]}

Maj, J ^{[1
]}

Mancini, D ^{[1
]}

Erdmann, J ^{[1
]}

Gaarde, P ^{[1
]}

机构：

[1] Argonne Natl Lab, Adv Photon Source, Argonne, IL 60439 USA

来源：

X-RAY OPTICS DESIGN, PERFORMANCE, AND APPLICATIONS | 1999年 / 3773卷

关键词：

x-ray monochromator; multilayers; graded;

D O I：

10.1117/12.370084

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

We describe a tunable multilayer monochromator with an adjustable bandpass to be used for reflectivity and grazing incidence diffraction studies on surfaces at energies near 10 keV. Multilayers have a bandpass typically 100 times larger than the Si (111)reflection, and by using multilayers an experimenter can significantly increase data collection rates over those available with a Si monochromator. The transmission through 1 and 2 laterally graded multilayer (LGML) reflections was recorded versus photon energy. The identical LGMLs were comprised of 60 bilayers of W and C on 100 x 25 x 3 mm float glass with a bilayer spacing varying from 35 to 60 Angstrom. The average gradient was 0.27 Angstrom/mm along the long dimension, The rms deviation of the data for the bilayer spacing from a linear fit was 0.36 Angstrom. Data were obtained for a nondispersive (+/-) double-multilayer arrangement. The relative bandpass width (FWHM) when the two multilayers exposed the same bilayer spacing was measured to be 2.2% with a transmission of 78.7 +/- 1.6%. This value is consistent with the transmission of 88.9% that we also measured for a single LGML at HASYLAB beamline D4. The bandpass was tunable in the range 1.1% to 2.2%.

引用

页码：100 / 106

页数：7