High-temperature oxidation behavior of sputtered IN 738 nanocrystalline coating

被引：32

作者：

Geng, SJ ^{[1
]}

Wang, FH ^{[1
]}

Zhu, SL ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China

来源：

OXIDATION OF METALS | 2002年 / 57卷 / 3-4期

基金：

中国国家自然科学基金;

关键词：

sputtering; IN; 738; alloy; nanocrystalline coating; oxidation;

D O I：

10.1023/A:1014870101143

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A sputtered nanocrystalline coating of IN 738 alloy was obtained by means of magnetron sputtering. The isothermal oxidation behavior at 800, 900, and 1000degreesC and the cyclic oxidation behavior at 950degreesC of the coating were studied in comparison with IN 738 cast alloy. The results indicated that a double external oxide scale was formed on the nanocrystalline coating at 900, 950, and 1000degreesC without internal oxide and nitride. The scale consisted in an outer mixture of Cr2O3, TiO2, and NiCr2O4 and an inner, continuous Al2O3 layer, which offered good adhesive and protectiveness. However, at 800degreesC a continuous Al2O3 scale could not be formed during oxidation of nanocrystalline coating and aluminum was still oxidized internally.

引用

页码：231 / 243

页数：13

共 13 条

[1] THE ROLE OF ALUMINUM AND TITANIUM ON THE OXIDATION PROCESS OF A NICKEL-BASE SUPERALLOY IN STEAM AT 800-DEGREES-C [J].

ABE, F ;

ARAKI, H ;

YOSHIDA, H ;

OKADA, M .

OXIDATION OF METALS, 1987, 27 (1-2) :21-36

[2] OXIDATION PROTECTION OF ALLOY IN-738-LC BY PLASMA ASSISTED VAPOR-DEPOSITED SILICA COATING [J].

BENNETT, MJ ;

TUSON, AT ;

KNIGHTS, CF ;

AYRES, CF .

MATERIALS SCIENCE AND TECHNOLOGY, 1989, 5 (08) :841-852

[3] NA2SO4-INDUCED AND NACL-INDUCED HOT CORROSION OF 6 NICKEL-BASE SUPERALLOYS [J].

BOURHIS, Y ;

JOHN, CS .

OXIDATION OF METALS, 1975, 9 (06) :507-528

[4] Effect of nanocrystallization on the oxide formation of Ni-5Cr-5Al alloy [J].

Chen, GF ;

Lou, HY .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1999, 18 (23) :1957-1959

[5]

Felix P, 1972, DEPOSITION CORROSION, P331

[6]

LOU HY, 1992, OXID MET, V38, P299, DOI 10.1007/BF00666917

[7] REHEALING ABILITY OF OXIDE SCALES FORMED ON MICROCRYSTALLINE K38G COATINGS [J].

LOU, HY ;

ZHU, SL ;

WANG, FH .

OXIDATION OF METALS, 1995, 43 (3-4) :317-328

[8] HIGH-TEMPERATURE OXIDATION OF COBALT-21 WT PERCENT CHROMIUM-3 VOL PERCENT Y2O3 ALLOYS [J].

STRINGER, J ;

WRIGHT, IG .

OXIDATION OF METALS, 1972, 5 (01) :59-&

[9]

WAGNER C, 1959, Z ELEKTROCHEM, V63, P772

[10] Effect of nanocrystallization on the corrosion resistance of K38G superalloy in CO+CO2 atmospheres [J].

Wang, FH ;

Young, DJ .

OXIDATION OF METALS, 1997, 48 (5-6) :497-509

← 1 2 →