Effect of Ca Content on Hot Tearing Susceptibility of Mg-4Zn-xCa-0.3Zr (x=0.5, 1, 1.5, 2) Alloys

被引:12
作者
Bai, Shengwei [1 ,2 ]
Wang, Feng [1 ,2 ]
Wang, Zhi [1 ,2 ]
Leng, Feng [1 ,2 ]
Liu, Zheng [1 ,2 ]
Mao, Pingli [1 ,2 ]
机构
[1] Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang, Peoples R China
[2] Key Lab Magnesium Alloys & Proc Technol Liaoning, Shenyang, Peoples R China
关键词
Mg– Zn– Ca– Zr alloy; hot tearing susceptibility; dendritic growth; microstructure; CRACKING;
D O I
10.1007/s40962-020-00553-9
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Mg-Zn-Ca alloy has a good development prospect in biomedical alloy. However, its development is restricted by large hot tearing susceptibility. Herein, the influence of Ca addition on the hot tearing susceptibility (HTS) of Mg-4Zn-xCa-0.3Zr (0.5, 1, 1.5, and 2 wt%) alloys has been studied by using thermal analysis and numerical simulation software, Procast. The "Clyne-Davies" hot tearing prediction model was improved, and Cracking Susceptibility Coefficient (CSC) was recalculated to highlight the physical significance of the model. The hot tearing zone was observed via optical microscopy and scanning electron microscopy, and the phase composition was analyzed with X-ray diffraction. The results of numerical simulations suggest that the Hot Tearing Indicator (HTI) tended to decrease with increase in Ca addition. However, the experimental results reveal that with the increase in Ca addition, the hot tearing susceptibility of the alloys first decreased with Ca addition up to 1.5 wt% and then displayed a slight increase with the addition up to 2.0 wt%. The SEM images and experimental results reveal that the thickness and ability to resist solidification shrinkage stress of the liquid membrane, quantity of the second phases, and feeding ability were all enhanced with the increase in Ca addition, thereby reducing the HTS of Mg-4Zn-XCa-0.3Zr alloys. When the Ca addition reached 2.0 wt%, the brittle calcium-containing phase forms at the grain boundary, which reduces the high-temperature strength of the matrix and the ability to resist the solidification shrinkage stress of the alloy, resulting in an increase in HTS. Therefore, when the Ca addition was 2.0 wt%, the simulation results were different from the experimental results.
引用
收藏
页码:1298 / 1308
页数:11
相关论文
共 29 条
[1]  
BORLAND JC, 1979, WELD MET FABR, V47, P99
[2]   Hot Cracking Susceptibility of Ternary Mg-Al-Ca Alloys [J].
Cao, G. ;
Kou, S. .
THERMEC 2006 SUPPLEMENT: 5TH INTERNATIONAL CONFERENCE ON PROCESSING AND MANUFACTURING OF ADVANCED MATERIALS, 2007, 15-17 :501-506
[3]  
Cao Y., 2016, STUDY MICROSTRUCTURE
[4]  
Chen LL, 2006, CAD CAE CAM TECHNOLO
[5]  
Clyne T.W., 1975, The British Foundryman, V68, P238
[6]   THE EFFECT OF MELT COMPOSITION ON SOLIDIFICATION CRACKING OF STEEL, WITH PARTICULAR REFERENCE TO CONTINUOUS-CASTING [J].
CLYNE, TW ;
WOLF, M ;
KURZ, W .
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1982, 13 (02) :259-266
[7]  
Ding Hao, 1997, Acta Metallurgica Sinica, V33, P921
[8]   Hot Tearing Susceptibility of AXJ530 Alloy Under Low-Frequency Alternating Magnetic Field [J].
Du, Xudong ;
Wang, Feng ;
Wang, Zhi ;
Li, Xingxing ;
Liu, Zheng ;
Mao, Pingli .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2020, 33 (09) :1259-1270
[9]  
Fu J, 2009, NUMERICAL SIMULATION
[10]   Effects of Sb Content on Solidification Pathways and Grain Size of AZ91 Magnesium Alloy [J].
Hou, Dan-Hui ;
Liang, Song-Mao ;
Chen, Rong-Shi ;
Dong, Chuang ;
Han, En-Hou .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2015, 28 (01) :115-121