Synthesis of high alumina ZSM-5 molecular sieve with ethylene diamine as template

被引:0
|
作者
Venkatathri, N. [1 ]
机构
[1] Natl Chem Lab, Catalysis Div, Pune 411008, Maharashtra, India
关键词
molecular sieve; zeolite; ethylenediamine;
D O I
暂无
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Attempts were made to investigate compositional constraints in the synthesis of pentasill molecular sieves, including aluminosilicate zeolites using ethylene diamine (C2DN) template, from the gel composition 1.85Na(2)O : aAl(2)O(3) : 15.2SiO(2) : 592H(2)O : 19.7C(2)DN in the temperature 177 degrees C for ten days. When a = 0.25 the product was ZSM-5 and then a = 1 the product was ZSM-35 and in between compositions the mixture of two were obtained. Reduce the time of crystallization time to 5 days give nanocrystalline material. XRD and FT-IR spectra in framework region of ZSM-5 synthesized using ethylene diamine template and without template are having similar pattern, however the intensity varies. Scanning electron microscopic picture of the both are varies. The structural stability of the zeolite ZSM-5 synthesized using no template was also found to be lower as compared with that for the ZSM-5 synthesized using ethylene diamine template. These differences. may result from the occluded excess sodium.
引用
收藏
页码:686 / 691
页数:6
相关论文
共 50 条
  • [41] Synthesis of ZSM-5 Membrane on the Anodized Alumina by Adding Promoter Ions
    S.H. Tsai
    T.G. Tsai
    H.C. Shih
    K.J. Chao
    Journal of Porous Materials, 1999, 6 : 127 - 133
  • [42] Synthesis and characterization of ZSM-5/MCM-41 meso/microporous composite molecular sieve incorporated by lanthanum
    Faculty of Material Science and Chemistry Engineering, China University of Geosciences, Wuhan 430074, China
    不详
    Diqiu Kexue Zhongguo Dizhi Daxue Xuebao, 2008, 1 (61-66):
  • [43] Synthesis of ZSM-5 membrane on the anodized alumina by adding promoter ions
    Tsai, SH
    Tsai, TG
    Shih, HC
    Chao, KJ
    JOURNAL OF POROUS MATERIALS, 1999, 6 (02) : 127 - 133
  • [44] INFLUENCE OF TEMPLATE ON CRYSTALLIZATION OF ZSM-5 ZEOLITES
    JOSHI, PN
    RAO, GN
    KOTASTHANE, AN
    SHIRALKAR, VP
    JOURNAL OF INCLUSION PHENOMENA AND MOLECULAR RECOGNITION IN CHEMISTRY, 1990, 9 (02): : 91 - 99
  • [45] Progress in preparation and application of short b-axis ZSM-5 molecular sieve
    Wang Z.
    Ke M.
    Li J.
    Li S.
    Sun J.
    Tong Y.
    Zhao Z.
    Liu J.
    Ren L.
    Huagong Xuebao/CIESC Journal, 2023, 74 (04): : 1457 - 1473
  • [46] A novel approach for the removal of radiocesium from aqueous solution by ZSM-5 molecular sieve
    Gao, Xiaoqing
    Zhang, Peng
    Yang, Junqiang
    Sun, Xuejie
    Fu, Yi
    Shi, Keliang
    Chai, Zhifang
    Wu, Wangsuo
    APPLIED RADIATION AND ISOTOPES, 2018, 139 : 231 - 237
  • [47] Preparation, surface acidity and catalytic performance of Beta/ZSM-5 composite molecular sieve
    Fan, Xiaojuan
    Zhang, Baoqiang
    Su, Ziyi
    Ma, Weihua
    CHEMICAL PHYSICS, 2022, 558
  • [48] Synthesis of high permeances of ZSM-5 zeolite membranes
    Li, YS
    Wang, JQ
    Guo, SC
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2000, 21 (12): : 1812 - 1814
  • [49] Lignin as a Bio-Sourced Secondary Template for ZSM-5 Zeolite Synthesis
    Flores, Camila Gomes
    Schneider, Helena
    Louis, Benoit
    CATALYSTS, 2022, 12 (04)
  • [50] Application of fractional factorial design to ZSM-5 synthesis using ethanol as template
    Zhang, Dongsheng
    Wang, Rijie
    Yang, Xiaoxia
    MICROPOROUS AND MESOPOROUS MATERIALS, 2009, 126 (1-2) : 8 - 13