Property degradation of tetragonal zirconia induced by low-temperature defect reaction with water molecules

被引:160
作者
Guo, X [1 ]
机构
[1] Forschungszentrum Julich, Inst Festkorperforsch, D-52425 Julich, Germany
关键词
D O I
10.1021/cm040167h
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Tetragonal ZrO2 exhibits good ionic conductivity, high strength, and fracture toughness. But while annealing at relatively low temperatures (63-400degreesC), tetragonal ZrO2 spontaneously transforms to a monoclinic one, and its electrical and mechanical properties degrade severely. The phenomenological observations of the low-temperature degradation of tetragonal ZrO2 are summarized, and major degradation mechanisms are critically reviewed. It is crucial to maintain sufficient oxygen vacancy concentration to stabilize the tetragonal structure; excess reduction of the oxygen vacancy concentration causes the tetragonal to monoclinic transformation. Water molecules can be incorporated into the ZrO2 lattice by filling oxygen vacancies, which leads to the formation of proton defects. Experimental and theoretical evidence support such a defect reaction between oxygen vacancies and water molecules. And a degradation mechanism based on this defect reaction satisfactorily explains all the phenomenological observations. The diffusion rate of oxygen vacancies at low temperatures is not high enough to cause the observed degradation depth; therefore, the relatively fast diffusion of proton defects most probably controls the degradation process.
引用
收藏
页码:3988 / 3994
页数:7
相关论文
共 128 条
[31]   Low temperature degradation mechanism of tetragonal zirconia ceramics in water: role of oxygen vacancies [J].
Guo, X .
SOLID STATE IONICS, 1998, 112 (1-2) :113-116
[32]   On the degradation of zirconia ceramics during low-temperature annealing in water or water vapor [J].
Guo, X .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1999, 60 (04) :539-546
[33]  
Guo X, 2000, PHYS STATUS SOLIDI A, V177, P191, DOI 10.1002/(SICI)1521-396X(200001)177:1<191::AID-PSSA191>3.0.CO
[34]  
2-X
[35]   Hydrothermal degradation mechanism of tetragonal Zirconia [J].
Guo, X .
JOURNAL OF MATERIALS SCIENCE, 2001, 36 (15) :3737-3744
[36]   Size dependent grain-boundary conductivity in doped zirconia [J].
Guo, X .
COMPUTATIONAL MATERIALS SCIENCE, 2001, 20 (02) :168-176
[37]   PHYSICAL ORIGIN OF THE INTRINSIC GRAIN-BOUNDARY RESISTIVITY OF STABILIZED-ZIRCONIA - ROLE OF THE SPACE-CHARGE LAYERS [J].
GUO, X .
SOLID STATE IONICS, 1995, 81 (3-4) :235-242
[38]   EFFECT OF STRESS-INDUCED PHASE-TRANSFORMATION ON PROPERTIES OF POLYCRYSTALLINE ZIRCONIA CONTAINING METASTABLE TETRAGONAL PHASE [J].
GUPTA, TK ;
LANGE, FF ;
BECHTOLD, JH .
JOURNAL OF MATERIALS SCIENCE, 1978, 13 (07) :1464-1470
[39]  
HECHT NL, 1986, SCI TECHNOLOGY ZIRCO, V3, P133
[40]   SUBEUTECTOID DEGRADATION OF YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTAL AND CERIA-DOPED YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTAL CERAMICS [J].
HERNANDEZ, MT ;
JURADO, JR ;
DURAN, P ;
FIERRO, JLG .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (06) :1254-1258