Crack closure effects during low cycle fatigue propagation in line pipe steel: An analysis with digital image correlation

被引：36

作者：

Rabbolini, S. ^{[1
]}

Beretta, S. ^{[1
]}

Foletti, S. ^{[1
]}

Cristea, M. E. ^{[2
]}

机构：

[1] Politecn Milan, Dept Mech Engn, I-20156 Milan, Italy

[2] Dalmine SpA, TenarisDalmine R&D Struct Integr Dept, I-24044 Dalmine, BG, Italy

来源：

ENGINEERING FRACTURE MECHANICS | 2015年 / 148卷

关键词：

Very low cycle fatigue; Crack propagation; Short cracks; Effective J-Integral; Crack-closure; Digital image correlation; HIGH-TEMPERATURE; OPENING LOADS; ROTOR STEELS; GROWTH; NOTCHES; BODIES; LCF;

D O I：

10.1016/j.engfracmech.2015.07.070

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Fatigue crack growth was investigated in a line pipe steel. Severe straining conditions, like those experienced by pipelines, were considered during the experiments. Crack closure effects were investigated during the tests by adopting an innovative technique based on digital image correlation. Experimentally measured crack closure levels were implemented in a crack propagation model based on elastic-plastic fracture mechanics. A modified formulation of Delta J(eff), necessary to accurately describe crack propagation driving forces, is presented and employed to assess fatigue life in presence of high plastic strains. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：441 / 456

页数：16

共 50 条

[31] Effect of hybrid reinforcement on crack initiation and early propagation mechanisms in cast metal matrix composites during low cycle fatigue
Iqbal, A. K. M. Asif
Arai, Yoshio
Araki, Wakako
MATERIALS & DESIGN, 2013, 45 : 241 - 252
[32] Using Barkhausen Noise and Digital Image Correlation to Investigate the Influence of Local Residual Stresses on Fatigue-Crack Propagation
Thielen, M.
Marx, M.
Sheikh-Amiri, M.
Boller, C.
Motz, C.
MATERIALS PERFORMANCE AND CHARACTERIZATION, 2016, 5 (03)
[33] Crack propagation analysis in bituminous mixtures reinforced by different types of geogrids using digital image correlation
Freire, Reuber Arrais
Di Benedetto, Herve
Sauzeat, Cedric
Pouget, Simon
Lesueur, Didier
CONSTRUCTION AND BUILDING MATERIALS, 2021, 303
[34] Experimental analysis of mode I crack propagation in adhesively bonded joints by optical backscatter reflectometry and comparison with digital image correlation
Lima, R. A. A.
Perrone, R.
Carboni, M.
Bernasconi, A.
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2021, 116
[35] Visualization of strain distribution around fatigue crack developed by low cycle fatigue test in high-strength steels using digital image correlation method for replica films
Koga, Norimitsu
Sakamaki, Yuta
Kaseya, Akihiro
Umezawa, Osamu
Nakata, Hiroshi
Toyoda, Shunsuke
MATERIALS CHARACTERIZATION, 2022, 185
[36] Digital image correlation analysis of crack initiation and failure in heat-treated granite during the Brazilian test
Yang, Zheyi
Wu, Jinwen
Cui, Zhehua
Qiu, Yongfeng
Song, Gaoying
Ma, Yiming
Feng, Zijun
Du, Menglin
Geng, Shaobo
Chen, Shuping
GEOTHERMICS, 2024, 121
[37] Experimental investigation of mixed mode I-II fatigue crack propagation in concrete using a digital image correlation method
Jia, Mengdi
Wu, Zhimin
Yu, Rena C.
Zhang, Xiaoxin
ENGINEERING FRACTURE MECHANICS, 2022, 272
[38] Three-dimensional characterization of low-cycle fatigue crack morphology in TRIP-maraging steel: Crack closure, geometrical uncertainty and wear
Zhang, Zhao
Koyama, Motomichi
Tsuzaki, Kaneaki
Noguchi, Hiroshi
INTERNATIONAL JOURNAL OF FATIGUE, 2021, 143
[39] Effect of microstructure on slip-induced crack initiation and early propagation of martensitic steel during high cycle fatigue
Dai, Yajun
Wang, Shijian
He, Qiyuan
Liu, Chang
Wang, Xianyu
Li, Xue
Li, Lang
Liu, Yongjie
He, Chao
Wang, Qingyuan
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 167
[40] In-situ observations of the effects of orientation and carbide on low cycle fatigue crack propagation in a single crystal superalloy
Ma, Xianfeng
Shi, Huiji
Gu, Jialin
Chen, Guofeng
Luesebrink, Oliver
Harders, Harald
FATIGUE 2010, 2010, 2 (01): : 2287 - 2295

← 1 2 3 4 5 →