Assessment of stress corrosion crack initiation and propagation in AISI type 316 stainless steel by electrochemical noise technique

被引：49
|
作者：
Anita, T. [1 ]
Pujar, M. G. [1 ]
Shaikh, H. [1 ]
Dayal, R. K. [1 ]
Khatak, H. S. [1 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Div, Kalpakkam 603102, Tamil Nadu, India
来源：
CORROSION SCIENCE | 2006年 / 48卷 / 09期
关键词：
stress corrosion cracking; pitting corrosion; visual records of current and potential; standard deviation; power spectral density;
D O I：
10.1016/j.corsci.2005.09.007
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Electrochemical noise (EN) analyses, using time domain, frequency domain and statistical parameters, were carried out on the potential and current data obtained on AISI type 316 stainless steel during (i) pitting corrosion in deaerated 0.5 M sodium chloride (NaCl) solution, and during (ii) stress corrosion cracking (SCC) in boiling acidified NaCl solution. Visual records and statistical analysis of the current and potential data alongwith the spectral estimation using maximum entropy method (MEM) gave useful informations on differentiating between these corrosion processes and on the effect of stress in accelerating pitting corrosion. The results correlated well with the optical microscopic observations. (c) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2689 / 2710
页数：22
相关论文
共 50 条
  • [21] Evaluation of stress corrosion cracking phenomenon in an AISI type 316LN stainless steel using acoustic emission technique
    Shaikh, H.
    Amirthalingam, R.
    Anita, T.
    Sivaibharasi, N.
    Jaykurnar, T.
    Manohar, P.
    Khatak, H. S.
    CORROSION SCIENCE, 2007, 49 (02) : 740 - 765
  • [22] Pitting and stress corrosion cracking studies on AISI type 316N stainless steel weldments
    Toppo, Anita
    Pujar, M. G.
    Sreevidya, N.
    Philip, John
    DEFENCE TECHNOLOGY, 2018, 14 (03): : 226 - 237
  • [23] Pitting and stress corrosion cracking studies on AISI type 316N stainless steel weldments
    Anita Toppo
    M.G.Pujar
    N.Sreevidya
    John Philip
    Defence Technology, 2018, (03) : 226 - 237
  • [24] Pitting and stress corrosion cracking studies on AISI type 316N stainless steel weldments
    Anita Toppo
    MGPujar
    NSreevidya
    John Philip
    Defence Technology, 2018, 14 (03) : 226 - 237
  • [25] THE CORROSION FATIGUE CRACK PROPAGATION OF 316LN AUSTENITIC STAINLESS STEEL
    Yang, Bin
    Wu, Huanchun
    7TH INTERNATIONAL CONFERENCE INTEGRITY-RELIABILITY-FAILURE (IRF2020), 2020, : 321 - 322
  • [26] Corrosion of AISI type 316 stainless steel in sodium and the assessment of long-term tensile behaviour
    Pillai, SR
    Khatak, HS
    Gnanamoorthy, JB
    MATERIALS TRANSACTIONS JIM, 1998, 39 (03): : 370 - 377
  • [27] AE response of type 304 stainless steel during stress corrosion crack propagation
    Alvarez, M. G.
    Lapitz, P.
    Ruzzante, J.
    CORROSION SCIENCE, 2008, 50 (12) : 3382 - 3388
  • [28] Determination of susceptibility to intergranular corrosion and electrochemical reactivation behaviour of AISI 316L type stainless steel
    Aydogdu, G. H.
    Aydinol, M. K.
    CORROSION SCIENCE, 2006, 48 (11) : 3565 - 3583
  • [29] Comparative analysis of electrochemical noise generated during stress corrosion cracking of AISI 304 stainless steel
    Leban, M
    Dolecek, V
    Legat, A
    CORROSION, 2000, 56 (09) : 921 - 927
  • [30] A mechanism for the crack initiation of corrosion fatigue of Type 316L stainless steel in Hank's solution
    Xie, JH
    Alpas, AT
    Northwood, DO
    MATERIALS CHARACTERIZATION, 2002, 48 (04) : 271 - 277
12345