Direct measurement of residual contact area and volume during the nanoindentation of coated materials as an alternative method of calculating hardness

被引:28
作者
Randall, NX [1 ]
机构
[1] CSEM Instruments, CH-2007 Neuchatel, Switzerland
来源
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES | 2002年 / 82卷 / 10期
关键词
D O I
10.1080/01418610210133504
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The mechanical properties of thin films can be measured by a variety of different techniques, with nanoindentation being one of the most recent developments in this growing field. By using a depth-sensing indentation method it is possible to obtain quantitative values for the hardness and modulus and thus to gain better insight into the response of a material to controlled deformation at such small scales. However, previous work by Tsui and Pharr has shown that the effects of pile-up, particularly in sofa films deposited on hard substrates, can produce significant overestimation of the hardness and modulus due to an underestimation of the true contact area by common nanoindentation analysis procedures. By measuring the topography of the residual indent using scanning force microscopy (SFM) and combining this information with the indentation data, it is possible to gain a fuller understanding of the indentation method and its effects on the material being tested. In addition, the true contact area can be directly measured from the SFM images and subsequently used to recalculate the hardness of the material more accurately. Moreover. the SFM allows the plastic volume of indentation to be measured, from which hardness can also be calculated in terms of plastic work. Experimental results are presented for two types of thin film deposited on hard substrates A here SFM analysis of indentations at various depths gives significant additional information concerning the true response of the system to instrumented indentation at a nanometric scale. Pile-up effects can be precisely. monitored as a function of depth and correlated to hardness variations encountered across the coating-substrate interface.
引用
收藏
页码:1883 / 1892
页数:10
相关论文
共 17 条
  • [1] Improvements in the indentation method with a surface force apparatus
    Bec, S
    Tonck, A
    Georges, JM
    Georges, E
    Loubet, JL
    [J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1996, 74 (05): : 1061 - 1072
  • [2] A method for interpreting the data from depth-sensing indentation instruments
    Doerner, M. F.
    Nix, W. D.
    [J]. JOURNAL OF MATERIALS RESEARCH, 1986, 1 (04) : 601 - 609
  • [3] A SIMPLE PREDICTIVE MODEL FOR SPHERICAL INDENTATION
    FIELD, JS
    SWAIN, MV
    [J]. JOURNAL OF MATERIALS RESEARCH, 1993, 8 (02) : 297 - 306
  • [4] Hainsworth SV, 1997, MATER RES SOC SYMP P, V436, P275
  • [5] Analysis of nanoindentation load-displacement loading curves
    Hainsworth, SV
    Chandler, HW
    Page, TF
    [J]. JOURNAL OF MATERIALS RESEARCH, 1996, 11 (08) : 1987 - 1995
  • [6] JENNET NM, 1995, P 9 INT S HARDN TEST, V1194, P201
  • [7] The effect of the indenter load on the nanohardness of ductile metals: an experimental study on polycrystalline work-hardened and annealed oxygen-free copper
    Lim, YY
    Chaudhri, MM
    [J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1999, 79 (12): : 2979 - 3000
  • [8] Do residual nano indentations in metals and ceramics relax with time?
    Lim, YY
    Chaudhri, MM
    [J]. JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2001, 34 (13) : L70 - L78
  • [9] LOUBET JL, 1986, NANOINDENTATION TECH, P7
  • [10] OLIVER WC, 1992, J MATER RES, V7, P1580