Sound absorbing properties of perforated composite panels of recycled rubber, fiberboard sawdust, and high density polyethylene

Recycled natural or synthetic polymers, typically waste rubber, may find their novel usage in the production of acoustic materials for their good impedance properties. To that end, rubber granules from used tires (R), high-density fiberboard flooring sawdusts (W), and fresh HDPE pellets (P) were fully blended at a proven mass ratio of 18, 40, and 42 percent, with 5 percent MA-PE as coupling agent based on W/R/P overall weight. The mixture was mould-pressed into composite panels at 185 degrees C for 20 min, under a pressure of 1 MPa. Small holes of 1 mm-6 mm in diameter were subsequently drilled at three perforation rates (3%, 6%, and 9%). Sound absorption testing was conducted with an impedance tube following ISO 10534-2 standard at incident sound frequencies from 63 Hz to 6300 Hz. To imitate a Helmholtz resonating structure, distance (D) between the perforated sample and the adjuster was set as 50 mm, 100 mm, and 150 mm, creating different cavity volumes. It was found that perforated WRPC panels have both high sound absorption coefficients and broad bandwidth, especially at frequencies lower than 1000 Hz. At higher frequencies range, hole size seemingly showed no evident influences while larger perforation rates produced higher sound absorption coefficients (SAC). The SAC-frequency curves showed 2, 4, and 6 peaks as D was 50 mm, 100 mm, and 150 mm, respectively, with half-peak bandwidth decreasing as frequency increases. The above results may supply helpful guidance to design WRPC acoustic materials. (C) 2018 Elsevier Ltd. All rights reserved.