Effects of Short-Time Tempering on Impact Toughness, Strength, and Phase Evolution of 4340 Steel Within the Tempered Martensite Embrittlement Regime

被引:19
作者
Euser, V. K. [1 ]
Williamson, D. L. [1 ]
Clarke, K. D. [1 ]
Findley, K. O. [1 ]
Speer, J. G. [1 ]
Clarke, A. J. [1 ]
机构
[1] Colorado Sch Mines, Golden, CO 80401 USA
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2019年 / 50A卷 / 08期
关键词
RETAINED AUSTENITE; IRON-CARBON; MICROSTRUCTURE; TEMPERATURE; CARBIDE; PRECIPITATION; REFINEMENT; MECHANISMS; CEMENTITE; METALS;
D O I
10.1007/s11661-019-05271-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
While tempering reactions under furnace conditions have been extensively studied, short-time tempering at higher temperatures, as might apply to induction tempering, has not been thoroughly explored. The mechanical behavior and phase development of short-time (1, 10, and 100seconds) and conventionally (3600seconds) tempered 4340 steel are compared at an equivalent degree of tempering defined by the Hollomon-Jaffe tempering parameter. The tempering parameter accurately predicts hardness values across short-time and conventional tempering conditions, but is less able to describe phase evolution associated with short-time tempering. Room temperature Charpy impact toughness and ductile-to-brittle transition temperature systematically improve with shorter tempering times at an equivalent tempering parameter. In particular, rapid tempering significantly increases toughness within the tempered martensite embrittlement regime. Relative to conventional tempering, shorter tempering times exhibit higher retained austenite content for a given tempering parameter, although no systematic or significant difference in cementite or transition carbide content is observed between time conditions. The retained austenite decomposition behavior indicates that the relationship between the classical tempering stages is altered at short tempering times, where increased overlap and/or re-ordering of stage II and III tempering are observed.
引用
收藏
页码:3654 / 3662
页数:9
相关论文
共 49 条
[1]  
[Anonymous], 2012, STAND TEST METH TENS
[2]  
[Anonymous], 1982, STAND METH NOTCH BAR
[3]   Tempering of Martensite in Dual-Phase Steels and Its Effects on Softening Behavior [J].
Baltazar Hernandez, V. H. ;
Nayak, S. S. ;
Zhou, Y. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (10) :3115-3129
[4]  
Bhadeshia H. K. D. H., 1979, Metal Science, V13, P325
[5]  
Byrer T.G., 1985, J. Heat Treat, V4, P39, DOI DOI 10.1007/BF02835488
[6]   THE TEMPERING OF IRON-CARBON MARTENSITE - DILATOMETRIC AND CALORIMETRIC ANALYSIS [J].
CHENG, L ;
BRAKMAN, CM ;
KOREVAAR, BM ;
MITTEMEIJER, EJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (10) :2415-2426
[7]   Atomic and nano scale chemical and structural changes in quenched and tempered 4340 steel [J].
Clarke, A. J. ;
Miller, M. K. ;
Field, R. D. ;
Coughlin, D. R. ;
Gibbs, P. J. ;
Clarke, K. D. ;
Alexander, D. J. ;
Powers, K. A. ;
Papin, P. A. ;
Krauss, G. .
ACTA MATERIALIA, 2014, 77 :17-27
[8]  
Clarke A.J., 2015, P INT C SOL SOL PHAS, P1107
[9]   ON THE TEMPERED MARTENSITE EMBRITTLEMENT IN AISI 4140 LOW-ALLOY STEEL [J].
DARWISH, FA ;
PEREIRA, LC ;
GATTS, C ;
GRACA, ML .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 132 :L5-L9
[10]  
Dieter G. E., 1986, MECH METALLURGY