Crack resistance properties of carbon nanotube-modified concrete

被引：51

作者：

Lan, Yingjia ^{[1
]}

Zheng, Bingmiao ^{[1
]}

Shi, Tao ^{[1
,2
]}

Ma, Chengchang ^{[1
]}

Liu, Yanming ^{[1
]}

Zhao, Zhifang ^{[1
]}

机构：

[1] Zhejiang Univ Technol, Coll Civil Engn, Hangzhou, Peoples R China

[2] Key Lab Civil Engn Struct & Disaster Prevent & Mi, Hangzhou, Peoples R China

来源：

MAGAZINE OF CONCRETE RESEARCH | 2022年 / 74卷 / 22期

基金：

中国国家自然科学基金;

关键词：

carbon nanotubes; composite materials; concrete; crack resistance; high-performance cementitious composites; FRACTURE-TOUGHNESS; MECHANICAL-PROPERTIES; CEMENT PASTE;

D O I：

10.1680/jmacr.21.00227

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Incorporating carbon nanotubes (CNTs) into concrete can improve its fracture toughness. The crack resistance properties of reinforced concrete with CNTs were tested by ring test and three-point bending beam fracture test. The fracture parameters of reinforced concrete with CNTs were analysed by using double-K fracture parameters and the results showed that CNTs can improve the crack resistance properties. When the CNT content was 0.10 wt%, the compressive strength at 28 days and the splitting tensile strength of concrete were increased by 1.7 and 11.7%, respectively. When the CNT content was 0.15 wt%, the cracking time of concrete under semi-closed and closed conditions was extended by 42.1 and 41.2%, respectively. The initiation fracture toughness, the unstable fracture toughness and the fracture energy of concrete were increased by 31.0, 32.4 and 24.6%, respectively. It was found that CNTs delay the propagation of micro-cracks by bridging across the micro-cracks in concrete and strengthening the interfacial transition zone.

引用

页码：1165 / 1175

页数：11

共 30 条

[11] Highly dispersed carbon nanotube reinforced cement based materials [J].

Konsta-Gdoutos, Maria S. ;

Metaxa, Zoi S. ;

Shah, Surendra P. .

CEMENT AND CONCRETE RESEARCH, 2010, 40 (07) :1052-1059

[12] Electrical transport in carbon nanotube fibres [J].

Lekawa-Raus, Agnieszka ;

Gizewski, Tomasz ;

Patmore, Jeff ;

Kurzepa, Lukasz ;

Koziol, Krzysztof K. .

SCRIPTA MATERIALIA, 2017, 131 :112-118

[13]

Li Gengying, 2005, Journal of the Chinese Ceramic Society, V33, P105

[14] Electrochemical impedance interpretation for the fracture toughness of carbon nanotube/cement composites [J].

Li, Wei-wen ;

Ji, Wei-ming ;

Fang, Guo-hao ;

Liu, Yu-qing ;

Xing, Feng ;

Liu, Yu-kai ;

Dong, Bi-qin .

CONSTRUCTION AND BUILDING MATERIALS, 2016, 114 :499-505

[15] Fracture toughness improvement of multi-wall carbon nanotubes/graphene sheets reinforced cement paste [J].

Liu, Jintao ;

Fu, Jiali ;

Ni, Tongyuan ;

Yang, Yang .

CONSTRUCTION AND BUILDING MATERIALS, 2019, 200 :530-538

[16]

[刘巧玲 Liu Qiaoling], 2020, [复合材料学报, Acta Materiae Compositae Sinica], V37, P952

[17] Autogenous Shrinkage and Crack Resistance of Carbon Nanotubes Reinforced Cement-Based Materials [J].

Liu, Yanming ;

Shi, Tao ;

Zhao, Yujing ;

Gu, Yuan ;

Zhao, Zhifang ;

Chen, Jiabin ;

Zheng, Bingmiao ;

Shi, Shichong .

INTERNATIONAL JOURNAL OF CONCRETE STRUCTURES AND MATERIALS, 2020, 14 (01)

[18] The influence of carbon nanotubes on the fracture energy, flexural and tensile behavior of cement based composites [J].

Rocha, Vanessa Vilela ;

Ludvig, Peter ;

Constancio Trindade, Ana Carolina ;

Silva, Flavio de Andrade .

CONSTRUCTION AND BUILDING MATERIALS, 2019, 209 :1-8

[19] Carbon nanotubes reinforced reactive powder concrete [J].

Ruan, Yanfeng ;

Han, Baoguo ;

Yu, Xun ;

Zhang, Wei ;

Wang, Danna .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2018, 112 :371-382

[20]

SAC, 2019, 500812019 GBT SAC

← 1 2 3 →