Plastic Zones at a Fatigue Crack Tip

被引：3

作者：

Gwider, Albashir ^{[1
]}

Ranganathan, Naryanaswami ^{[1
]}

机构：

[1] Polytech Tours, Lab Gabriel Lame, EA 7494, 7 Ave Marcel Dassault, F-37200 Tours, France

来源：

JOURNAL OF FAILURE ANALYSIS AND PREVENTION | 2019年 / 19卷 / 03期

关键词：

Aluminum; Fatigue analysis; Fatigue crack growth; Nanoindentation; Plastic zone; CRITERION;

D O I：

10.1007/s11668-019-00646-6

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Nanoindentation measurements are carried out in the fatigue plastic zone in the 2024 T351 alloy. It is shown that variations in hardness, plastic work and plasticity index show typical evolution permitting the identification of cyclic and monotonic plastic zones. The measured values are comparable with theoretical estimations. A calibration test permits the evolution of strains in the plastic zone.

引用

页码：673 / 681

页数：9

共 14 条

[1] FATIGUE CRACK-PROPAGATION IN MARTENSITIC AND AUSTENITIC STEELS [J].

BATHIAS, C ;

PELLOUX, RM .

METALLURGICAL TRANSACTIONS, 1973, 4 (05) :1265-1273

[2]

Beake BD, 2015, MAT CHARACTERIZATION

[3] The minimum plastic zone radius criterion for crack initiation direction applied to surface cracks and through-cracks under mixed mode loading [J].

Bian, LC ;

Kim, KS .

INTERNATIONAL JOURNAL OF FATIGUE, 2004, 26 (11) :1169-1178

[4] Role of plastic zone in crack growth direction criterion under mixed mode loading [J].

Golos, K ;

Wasiluk, B .

INTERNATIONAL JOURNAL OF FRACTURE, 2000, 102 (04) :341-353

[5]

Jendhoubi K, 1987, MESURES LOCALES GLOB

[6] Analysis of mixed mode crack initiation angles under various loading conditions [J].

Khan, SMA ;

Khraisheh, MK .

ENGINEERING FRACTURE MECHANICS, 2000, 67 (05) :397-419

[7] A new criterion for mixed mode fracture initiation based on the crack tip plastic core region [J].

Khan, SMA ;

Khraisheh, MK .

INTERNATIONAL JOURNAL OF PLASTICITY, 2004, 20 (01) :55-84

[8] An analysis of nanoindentation in elasto-plastic solids [J].

Poon, B. ;

Rittel, D. ;

Ravichandran, G. .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2008, 45 (25-26) :6399-6415

[9] Effect of actual and accelerated ageing on microstructure evolution and mechanical properties of a 2024-T351 aluminium alloy [J].

Prudhomme, M. ;

Billy, F. ;

Alexis, J. ;

Benoit, G. ;

Hamon, F. ;

Larignon, C. ;

Odemer, G. ;

Blanc, C. ;

Henaff, G. .

INTERNATIONAL JOURNAL OF FATIGUE, 2018, 107 :60-71

[10]

Ranganathan N., 1985, THESIS

← 1 2 →