Microstructural study of aluminum phosphate-sealed, plasma-sprayed chromium oxide coating

Microstructural characterization of aluminum phosphate-sealed, plasma-sprayed chromium oxide coating was carried out in order to study the strengthening mechanisms of the aluminum phosphate sealant in the coating. Characterization was performed using x-ray diffractometry, scanning electron microscopy, and analytical transmission electron microscopy. The structure of the sealed coating was lamellar with columnar alpha-Cr2O3 grains extending through the lamella thickness. Amorphous aluminum phosphate sealant had penetrated into the structural defects of the coating such as cracks, gaps, and pores between the lamellae. The relative composition was 25 at.% aluminum and 75 at.% phosphorus for the sealant in the coating, giving the molar ratio P/Al of 3, which corresponds to that of metaphosphates Al(PO3)(3). There is no indication of reaction products from the chemical reactions between the sealant and the coating. Thus, the aluminum phosphate sealing in the chromium oxide coatings can be explained mainly by adhesive binding resulting from the formation of the condensed phosphates with the appropriate adhesive properties to the coating, and not by chemical bonding resulting from the chemical reactions between the sealant and the coating.