Mechanical properties of alumina-metal-zirconia nano-micro hybrid composites

被引：6

作者：

Laurent, C ^{[1
]}

Rousset, A ^{[1
]}

Bonneford, P ^{[1
]}

Oquab, D ^{[1
]}

Lavelle, B ^{[1
]}

机构：

[1] INST NATL POLYTECH TOULOUSE,MAT LAB,URA CNRS 445,F-31077 TOULOUSE,FRANCE

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 1996年 / 16卷 / 09期

关键词：

D O I：

10.1016/0955-2219(96)00008-8

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Al2O3 and Al2O3-2 wt% Fe0.8Cr0.2 nanocomposite powders were wet-mixed with different ZrO2 or Y-ZrO2 powders. The influence of the ball-milling medium and mixing duration on the microstructure and the amount of tetragonal zirconia retained after hot-pressing are discussed. The fracture strength and fracture toughness of the alumina-metal-zirconia specimens ave lower than that of the alumina-metal and alumina-zirconia composites. This could result from a partial annihilation of the different reinfor cement mechanisms involved and also from interactions between zirconia and the metallic phase. There is no correlation between the mechanical properties and the amount of tetragonal zirconia. However, the amount of tetragonal to monoclinic transformation at the surface of the specimens during grinding prior to the mechanical tests seems to be a key parameter. (C) 1996 Elsevier Science Limited.

引用

页码：937 / 943

页数：7

共 31 条

[1] ON THE SOLUBILITY OF FE, CR AND NB IN ZRO2 AND ITS EFFECT ON THERMAL DILATION AND POLYMORPHIC TRANSITION [J].

BECK, HP ;

KALIBA, C .

MATERIALS RESEARCH BULLETIN, 1990, 25 (09) :1161-1168

[2]

BLEIER A, 1988, MATERIALS RES SOC S, V121, P145

[3] SOL-GEL PREPARED NI-ALUMINA COMPOSITE-MATERIALS .1. MICROSTRUCTURE AND MECHANICAL-PROPERTIES [J].

BREVAL, E ;

DENG, Z ;

CHIOU, S ;

PANTANO, CG .

JOURNAL OF MATERIALS SCIENCE, 1992, 27 (06) :1464-1468

[4] MICROSTRUCTURE OF ZIRCONIA-TOUGHENED ALUMINA OBTAINED THROUGH DIFFERENT PRECURSOR ROUTES [J].

BRODHAG, C ;

BACH, JP ;

THEVENOT, F ;

DELETTER, M .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 109 :53-59

[5]

BROWN WF, 1966, ASTM SPEC TECH PUB, V410

[6]

CARLSTROM E, 1984, J AM CERAM SOC, V67, pC169, DOI 10.1111/j.1151-2916.1984.tb19186.x

[7] IRON ALUMINA INTERFACE IN CERAMIC MATRIX NANOCOMPOSITES [J].

DEVAUX, X ;

LAURENT, C ;

BRIEU, M ;

ROUSSET, A .

JOURNAL OF ALLOYS AND COMPOUNDS, 1992, 188 (1-2) :179-181

[8]

DEVAUX X, 1991, CR ACAD SCI II, V312, P1425

[9]

Devaux X., 1993, Nanostructured Materials, V2, P339, DOI 10.1016/0965-9773(93)90174-A

[10]

DEVAUX X, 1992, COMPOSITE MATERIALS, P209

← 1 2 3 4 →