A distribution model of ultra-high cycle fatigue property based on crack density for braided CFRP

被引：3
作者：
Wu, Tao [1 ]
Yao, Weixing [2 ]
Xu, Chao [1 ]
机构：
[1] Nanjing Univ Aeronaut & Astronaut, Key Lab Fundamental Sci Natl Def Adv Design Techn, Nanjing 210016, Peoples R China
[2] Nanjing Univ Aeronaut & Astronaut, State Key Lab Mech & Control Mech Struct, Nanjing 210016, Peoples R China
来源：
COMPOSITE STRUCTURES | 2021年 / 256卷
关键词：
CFRP; Ultra-high cycle fatigue; Matrix crack; Probability density distribution; LIFE DISTRIBUTION; STATIC STRENGTH;
D O I：
10.1016/j.compstruct.2020.113037
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The microscopic observation and statistical investigation of matrix cracks are carried out through the ultra-high cycle bending fatigue experiment of braided CFRP (Carbon Fiber Reinforced Plastic) in this paper, and the matrix crack development law of CFRP under ultra-high cycle fatigue load has been studied. It is found that there are two different forms of matrix cracks under the ultra-high cycle fatigue load, and a bimodal distribution model of matrix crack density is established based on the distribution law of matrix crack density. At the same time, the ultra-high cycle fatigue life distribution model of braided CFRP is established based on the matrix crack density distribution model. At last, the corresponding fatigue life of CDS (Characteristic damage state) is obtained through the crack density evolution curve, and the life distribution model is verified.
引用
收藏
页数：6
相关论文
共 13 条
[1]  
Dong C., 1996, STRENGTH ENV, V3, P1
[2]  
Fougères R, 2002, AM SOC TEST MATER, V1419, P197
[3]   Fatigue testing of carbon fibre reinforced polymers under VHCF loading [J].
Gude, M. ;
Hufenbach, W. ;
Koch, I. ;
Koschichow, R. ;
Schulte, K. ;
Knoll, J. .
MATERIALS SCIENCE ENGINEERING, SYMPOSIUM B6 - HYBRID STRUCTURES, 2013, 2 :18-24
[4]   High-cycle fatigue characteristics of quasi-isotropic CFRP laminates over 108 cycles (Initiation and propagation of delamination considering interaction with transverse cracks) [J].
Hosoi, Atsushi ;
Sato, Narumichi ;
Kusumoto, Yasuyuki ;
Fujiwara, Keita ;
Kawada, Hiroyuki .
INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (01) :29-36
[5]   Fatigue strength of carbon fibre composites up to the gigacycle regime (gigacycle-composites) [J].
Michel, SA ;
Kieselbach, R ;
Martens, HJ .
INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (03) :261-270
[6]   Markov model of connection between the distribution of static strength and fatigue life of a fibrous composite [J].
Paramonov, Yu. ;
Kleinhof, M. ;
Paramonova, A. .
MECHANICS OF COMPOSITE MATERIALS, 2006, 42 (05) :431-442
[7]   LOGNORMAL-DISTRIBUTION - MODEL FOR FATIGUE LIFE AND RESIDUAL STRENGTH OF COMPOSITE-MATERIALS [J].
RATNAPARKHI, MV ;
PARK, WJ .
IEEE TRANSACTIONS ON RELIABILITY, 1986, 35 (03) :312-315
[8]  
Wu FQ, 2008, CHINESE J AERONAUT, V21, P241, DOI 10.1016/S1000-9361(08)60031-X
[9]   A natural frequency degradation model for very high cycle fatigue of woven fiber reinforced composite [J].
Wu, Tao ;
Yao, Weixing ;
Xu, Chao ;
Li, Piao .
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134
[10]   A VHCF life prediction method based on surface crack density for FRP [J].
Wu, Tao ;
Yao, Weixing ;
Xu, Chao .
INTERNATIONAL JOURNAL OF FATIGUE, 2018, 114 :51-56
12