Electrochemical behaviour of amino alcohol-based inhibitors used to control corrosion of reinforcing steel

被引：97
作者：
Jamil, HE
Shriri, A
Boulif, R
Bastos, C
Montemor, MF [1 ]
Ferreira, MGS
机构：
[1] Inst Super Tecn, Dept Chem Engn, Lisbon, Portugal
[2] Univ Kenitra, Kenitra, Morocco
[3] CERPHOS, Lab Rech Mat, Casablanca, Morocco
[4] Univ Aveiro, Dept Ceram & Glasses Engn, P-3800 Aveiro, Portugal
来源：
ELECTROCHIMICA ACTA | 2004年 / 49卷 / 17-18期
关键词：
organic inhibitors; corrosion; reinforced concrete; electrochemical impedance; SVET;
D O I：
10.1016/j.electacta.2004.01.041
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Laboratory investigations were performed in order to compare the electrochemical behaviour of amino alcohol-based inhibitors currently used to prevent (preventive inhibitors) and to control (curative inhibitor) corrosion of steel in concrete, respectively. The investigation was performed in the presence of chloride ions, using extract solutions simulating the concrete interstitial electrolyte. Electrochemical measurements allowed to compare the protective efficiency of these inhibitors. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2753 / 2760
页数：8
相关论文
共 18 条
  • [1] Effect of rebar cleanliness and repair materials on reinforcement corrosion and flexural strength of repaired concrete beams
    Al-Dulaijan, SU
    Ai-Zahrani, MM
    Saricimen, H
    Maslehuddin, M
    Shameem, M
    Abbasi, TA
    [J]. CEMENT & CONCRETE COMPOSITES, 2002, 24 (01) : 139 - 149
  • [2] BDJEGOVIC D, 1994, CORROSION CORROSION, P865
  • [3] Buffenbarger J.K., 2000, P INT C ADV MAT THEI
  • [4] Cigna R., 1994, CORROSION CORROSION, P878
  • [5] The application of electrochemical impedance spectroscopy to determine the long-term effectiveness of corrosion inhibitors for steel in concrete
    Dhouibi, L
    Triki, E
    Raharinaivo, A
    [J]. CEMENT & CONCRETE COMPOSITES, 2002, 24 (01) : 35 - 43
  • [6] Migrating corrosion inhibitor blend for reinforced concrete:: Part 2 -: Inhibitor as repair strategy
    Elsener, B
    Büchler, M
    Stalder, F
    Böhni, H
    [J]. CORROSION, 2000, 56 (07) : 727 - 732
  • [7] Migrating corrosion inhibitor blend for reinforced concrete:: Part 1 -: Prevention of corrosion
    Elsener, B
    Büchler, M
    Stalder, F
    Böhni, H
    [J]. CORROSION, 1999, 55 (12) : 1155 - 1163
  • [8] ELSENER B, 2000, P COST 521 WORKSH, V271
  • [9] Kinetics of self-assembled layer formation on iron
    Felhösi, I
    Telegdi, J
    Pálinkás, G
    Kálmán, E
    [J]. ELECTROCHIMICA ACTA, 2002, 47 (13-14) : 2335 - 2340
  • [10] An electrochemical and analytical approach to the inhibition mechanism of an amino-alcohol-based corrosion inhibitor for reinforced concrete
    Jamil, HE
    Montemor, MF
    Boulif, R
    Shriri, A
    Ferreira, MGS
    [J]. ELECTROCHIMICA ACTA, 2003, 48 (23) : 3509 - 3518
12