Effect of Thermal History on Microstructures and Mechanical Properties of AZ31 Magnesium Alloy Prepared by Friction Stir Processing

被引:57
作者
Chai, Fang [1 ]
Zhang, Datong [1 ]
Li, Yuanyuan [1 ]
机构
[1] S China Univ Technol, Natl Engn Res Ctr Near Net Shape Forming Metall M, Guangzhou 510640, Guangdong, Peoples R China
来源
MATERIALS | 2014年 / 7卷 / 03期
关键词
AZ31 magnesium alloy; friction stir processing; thermal history; microstructure; mechanical properties; CHANNEL ANGULAR EXTRUSION; AL-ZN ALLOY; DYNAMIC RECRYSTALLIZATION; TENSILE BEHAVIOR; 2024; ALUMINUM; GRAIN-SIZE; SUPERPLASTICITY; DEFORMATION; STRENGTH; IMPROVEMENT;
D O I
10.3390/ma7031573
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Hot-rolled AZ31 (Mg-2.57Al-0.84Zn-0.32Mn, in mass percentage) magnesium alloy is subjected to friction stir processing in air (normal friction stir processing, NFSP) and under water (submerged friction stir processing, SFSP). Thermal history of the two FSP procedures is measured, and its effect on microstructures and mechanical properties of the experimental materials is investigated. Compared with NFSP, the peak temperature during SFSP is lower and the duration time at a high temperature is shorter due to the enhanced cooling effect of water. Consequently, SFSP results in further grain refinement, and the average grain size of the NFSP and SFSP specimens in the stir zone (SZ) are 2.9 mu m and 1.3 mu m, respectively. Transmission electron microscopy (TEM) examinations confirm that grain refinement is attributed to continuous dynamic recrystallization both for NFSP and SFSP. The average Vickers hardness in the SZ of the NFSP and SFSP AZ31 magnesium alloy are 76 HV and 87 HV. Furthermore, the ultimate tensile strength and the elongation of the SFSP specimen increase from 191 MPa and 31.3% in the NFSP specimen to 210 MPa and 50.5%, respectively. Both the NFSP and SFSP alloys fail through ductile fracture, but the dimples are much more obvious in the SFSP alloy.
引用
收藏
页码:1573 / 1589
页数:17
相关论文
共 45 条
[1]   PRECIPITATION HARDENING [J].
ARDELL, AJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (12) :2131-2165
[2]   Low-temperature friction-stir welding of 2024 aluminum [J].
Benavides, S ;
Li, Y ;
Murr, LE ;
Brown, D ;
McClure, JC .
SCRIPTA MATERIALIA, 1999, 41 (08) :809-815
[3]   Producing nanograined microstructure in Mg-Al-Zn alloy by two-step friction stir processing [J].
Chang, C. I. ;
Du, X. H. ;
Huang, J. C. .
SCRIPTA MATERIALIA, 2008, 59 (03) :356-359
[4]   Achieving ultrafine grain size in Mg-Al-Zn alloy by friction stir processing [J].
Chang, C. I. ;
Du, X. H. ;
Huang, J. C. .
SCRIPTA MATERIALIA, 2007, 57 (03) :209-212
[5]   On the hardening of friction stir processed Mg-AZ31 based composites with 5-20% nano-ZrO2 and nano-SiO2 particles [J].
Chang, C. I. ;
Wang, Y. N. ;
Pei, H. R. ;
Lee, C. J. ;
Huang, J. C. .
MATERIALS TRANSACTIONS, 2006, 47 (12) :2942-2949
[6]   Relationship between grain size and Zener-Holloman parameter during friction stir processing in AZ31 Mg alloys [J].
Chang, CI ;
Lee, CJ ;
Huang, JC .
SCRIPTA MATERIALIA, 2004, 51 (06) :509-514
[7]  
Darras B., 2012, MATER DESIGN, V47, P133
[8]   Friction stir processing of commercial AZ31 magnesium alloy [J].
Darras, B. M. ;
Khraisheh, M. K. ;
Abu-Farha, F. K. ;
Omar, M. A. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 191 (1-3) :77-81
[9]   Improvement of strength of magnesium alloy processed by equal channel angular extrusion [J].
Ding, S. X. ;
Lee, W. T. ;
Chang, C. P. ;
Chang, L. W. ;
Kao, P. W. .
SCRIPTA MATERIALIA, 2008, 59 (09) :1006-1009
[10]   Using friction stir processing to produce ultrafine-grained microstructure in AZ61 magnesium alloy [J].
Du Xing-hao ;
Wu Bao-lin .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (03) :562-565