Effect of heat treatment on the distribution and volume fraction of Mg2Si in structural aluminum alloy 6063

被引：10
作者：
Al-Marahleh, C. [1 ]
机构：
[1] Al Balqa Appl Univ, Fac Engn, Dept Mat & Met Engn, Al Salt, Jordan
来源：
METAL SCIENCE AND HEAT TREATMENT | 2006年 / 48卷 / 5-6期
关键词：
Aluminum Alloy; Vickers Microhardness; Cast State; Final Aging; Extrusion Press;
D O I：
10.1007/s11041-006-0071-5
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The structure and properties of an aluminum alloy after extrusion in cast and homogenized states are studied. Commercial billets are melted in a horizontal continuous casting installation. After homogenizing the billets are used for fabricating shapes of specified form in an extrusion press. The shapes are subjected to final aging. The volume fraction and the distribution of the second Mg2Si phase are determined after different kinds of treatment. The structure and mechanical properties of shapes obtained from cast and homogenized billets are compared after aging and without aging. The effect of homogenizing on the properties of the alloy after extrusion is analyzed.
引用
收藏
页码：205 / 209
页数：5
相关论文
共 50 条
[21]   Brazing of graphite to 6063 aluminum alloy with Al-Cu-Si-Ni-Mg filler metal and Ag-Cu-Ti paste [J].
Yuan, Linlin ;
Wang, Wei ;
Chen, Xiaoyu ;
Huang, Xiaomeng ;
Qi, Yuefeng .
WELDING IN THE WORLD, 2021, 65 (06) :1211-1216
[22]   Brazing of graphite to 6063 aluminum alloy with Al-Cu-Si-Ni-Mg filler metal and Ag-Cu-Ti paste [J].
Linlin Yuan ;
Wei Wang ;
Xiaoyu Chen ;
Xiaomeng Huang ;
Yuefeng Qi .
Welding in the World, 2021, 65 :1211-1216
[23]   Effect of casting cooling rate on microstructure and hot workability of Al-Mg-Si-Mn heat-resistant aluminum alloy [J].
Qian X.-M. ;
Zhang Y. ;
Wang Z.-D. ;
Li Y. ;
Xu G.-M. ;
Wang H.-Y. .
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2022, 32 (02) :343-352
[24]   Effect of Metastable Mg2Si and Dislocations on α-Al(MnFe)Si Dispersoid Formation in Al-Mn-Mg 3xxx Alloys [J].
Li, Zhen ;
Zhang, Zhan ;
Chen, X-Grant .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (11) :5799-5814
[25]   Effect of Heat Treatment on Mechanical Properties and Fracture Behavior of Al-7.0Si-0.3Mg Alloy at Low Temperature [J].
Ma, Guanghui ;
Yang, Mengmeng ;
Geng, Zhe ;
Ding, Yunpeng ;
Liu, Hai ;
Jin, Yujing .
CRYSTALS, 2022, 12 (04)
[26]   Effect of aging treatment on the microstructure and flow behavior of 6063 aluminum alloy compressed over a wide range of strain rate [J].
Ye, Tuo ;
Li, Luoxing ;
Guo, Pengcheng ;
Xiao, Gang ;
Chen, Ziming .
INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2016, 90 :72-80
[27]   HEAT TREATMENT EFFECT ON THE INTERMETALLIC Al-Fe-Si ALLOY MICROSTRUCTURE [J].
Andreyachshenko, Violetta ;
Ulyeva, Gulnara .
ACTA METALLURGICA SLOVACA, 2024, 30 (04) :156-160
[28]   Effect of heat treatment conditions on microstructure and wear behaviour of A14Cu2Ni2Mg alloy [J].
Karakulak, Erdem ;
Zeren, Muzaffer ;
Yamanoglu, Ridvan .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (07) :1898-1904
[29]   Biaxial formability and microstructure of an Al-Mg-Si alloy sheet post solution heat treatment [J].
Fan, Xiaobo ;
Wang, Xugang ;
Lin, Yanli ;
He, Zhubin ;
Yuan, Shijian .
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 902
[30]   Effect of post-sealing treatment with different concentrations of NaH2PO4 on corrosion resistance of MAO coating on 6063 aluminum alloy [J].
Qin, Gemei ;
Zhang, Youcai ;
Yang, Erhui ;
Peng, Zhaowei ;
Wei, Wu ;
Xie, Xiaomeng ;
Li, Weizhou .
SURFACE & COATINGS TECHNOLOGY, 2022, 443
12345