Formation of Ni-Al and Ni-Al-X phases by mechanical alloying

被引:7
作者
Blinov, AM [1 ]
Portnoy, VK [1 ]
Kaloshkin, SD [1 ]
Tomilin, IA [1 ]
机构
[1] Moscow State Steel & Alloys Inst, Dept Phys Chem, Moscow 119049, Russia
来源
ISMANAM 2003: METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS | 2004年 / 20-21卷
关键词
additions; high temperature alloys; Ni-Al;
D O I
10.4028/www.scientific.net/JMNM.20-21.151
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The Ni-Al phases were synthesized in the composition range 40-85 at. % Ni by mechanical alloying (MA) of elemental component mixtures. MA of Ni-Al powders produces the B2 phase in the range 40 - 61 at. % Ni and a solid solution Ni(Al) - in the range 65-85 at. % Ni. Milling of Ni62.5Al37.5 composition results in formation of the B2 and Ni(Al) phases mixture. Formation of a supersaturated solid solution for 65-75 at. % Ni were accompanied by appearance of B2 phase at the intermediate MA stage. Ball milling of Ni and Al powder mixtures of the compositions corresponded to intermetallics NiAl and Ni3Al, with a 5 at. % addition of X=Ti, Mo or Nib, where the third element was substituted for Ni (Ni45Al50X5 and Ni70Al25X5), Al (Ni50Al45X5 and Ni75Al20X5) or both (Ni47.5Al47.5X5 and Ni71.25Al23.75X5) was performed. The regularities of influence of the third components on the final structure of the as-milled and annealed alloys were observed. The preferred sublattices for X additions in B2 and L1(2) intermetallic phases were determined.
引用
收藏
页码:151 / 156
页数:6
相关论文
共 8 条
[1]   ATOMIC DISTRIBUTION OF ALLOYING ADDITIONS BETWEEN SUBLATTICES IN THE INTERMETALLIC COMPOUNDS NI3AL AND NIAL .2. MICROSCOPIC CALCULATIONS AND X-RAY-DIFFRACTION ANALYSIS [J].
ALLAVERDOVA, NV ;
PORTNOY, VK ;
KUCHERENKO, LA ;
RUBAN, AV ;
BOGDANOV, VI .
JOURNAL OF THE LESS-COMMON METALS, 1988, 141 (02) :191-200
[2]   MECHANICALLY DRIVEN DISORDER AND PHASE-TRANSFORMATIONS IN ALLOYS [J].
BAKKER, H ;
ZHOU, GF ;
YANG, H .
PROGRESS IN MATERIALS SCIENCE, 1995, 39 (03) :159-241
[3]   Atomic size effects in Ni-Al based solid solutions [J].
Kitabjian, PH ;
Nix, WD .
ACTA MATERIALIA, 1998, 46 (02) :701-710
[4]   MECHANICAL ALLOYING OF THE NI-AL(M) (M TI, FE) SYSTEM [J].
LIU, ZG ;
GUO, JT ;
HU, ZQ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 192 :577-582
[5]   Ternary site preference energies, size misfits and solid solution hardening in NiAl and FeAl [J].
Medvedeva, NI ;
Gornostyrev, YN ;
Novikov, DL ;
Mryasov, ON ;
Freeman, AJ .
ACTA MATERIALIA, 1998, 46 (10) :3433-3442
[6]   ALLOYING BEHAVIOR AND MECHANICAL-PROPERTIES OF POLYCRYSTALLINE NI3AL (GAMMA-= PHASE) WITH TERNARY ADDITIONS [J].
RAWLINGS, RD ;
STATONBEVAN, AE .
JOURNAL OF MATERIALS SCIENCE, 1975, 10 (03) :505-514
[7]   Mechanical alloying and milling [J].
Suryanarayana, C .
PROGRESS IN MATERIALS SCIENCE, 2001, 46 (1-2) :1-184
[8]   FURTHER STUDIES ON NICKEL-ALUMINUM SYSTEM .1. BETA-NIAL AND DELTA-NI2AL3 PHASE FIELDS [J].
TAYLOR, A ;
DOYLE, NJ .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1972, 5 (JUN1) :201-&