Formation of (111) recrystallization texture in Al-Mg alloys

被引：2

作者：

Kamijo, T

Iwasaki, Y

Fukutomi, H

机构：

来源：

GRAIN GROWTH IN POLYCRYSTALLINE MATERIALS II, PTS 1 AND 2 | 1996年 / 204-卷

关键词：

Al-Mg alloy; warm-rolling; shear texture; (111)[(1)over-bar10] orientation; (111) recrystallization texture; r value; automobile;

D O I：

10.4028/www.scientific.net/MSF.204-206.371

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Al-4.0Mg and Al-5.5Mg alloys were warm-rolled to 85% at the temperatures ranging from 523K to 573K. The (001)[110] shear texture was formed in the surface of the sheets rolled below 543K. The (111)[<(1)over bar 10>] or the (112)[<(1)over bar 10>] shear texture with the spread around the rolling direction developed in the sheets rolled above 553K. After annealing the complicated recrystallization texture containing the (111) component parallel to the. rolling plane was generated in the sheets rolled above 553K. Such recrystallization texture was penetrated deeper into the inward layer with an increase in rolling temperature.

引用

页码：371 / 378

页数：8