Electrostatic and electrosteric stabilization of aqueous suspensions of barite nanoparticles

Electrostatic and electrosteric stabilization of aqueous suspensions of barite nanoparticles were investigated. The state of dispersion was evaluated in terms of zeta potential, apparent viscosity and the mean particle size of solid phase in the solution. Zeta potential, apparent viscosity and the mean particle size as a function of pH were performed in absence of dispersant. The result showed that electrostatic stabilization of the aqueous suspension of barite nanoparticles can be accomplished in low acidic and high basic range of pH. In presence of sodium polyacrylate (PAA-Na) dispersant, the isoelectric point (IEP) of the barite nanoparticles was shifted to lower pH and the negative zeta potential was increased in a large range of pH above the (IEP). The optimum amount of PAA-Na dispersant is discussed in the light of zeta potential and viscosity. It is found that the adsorption of PAA is correlated to the net surface charge of the barite nanoparticles and the fraction of dissociated polymer at pH 4, 8.5 and 10. At pH 4, the state of dispersion was achieved at higher amount of electrolyte due to the low fraction of negatively charged dissociated polymer and the positively charge particles. At basic pH, the fraction of dissociated polymer was high and the surface charge of particle was highly negative, therefore, the lowest viscosity was obtained at a small amount of PAA. In addition, the optimum amount of polymer decreased with the increase in pH of the suspension. (C) 2008 Published by Elsevier B.V.