Sintering and Performance of MgO from Bischofite with ZrO2 Additive

Effect of ZrO2 on sintering properties of MgO prepared from natural brine from Qarhan Salt Lake, crystalline bischofite and MgCl2 center dot 6H(2)O(AR) was studied. The results showed that ZrO2 of addition exceeded 1 wt% had promotive effect on sintering of magnesia prepared from MgCl2 center dot 6H(2)O(AR). While 1.5 wt% ZrO2 was added, the bulk density of sample was 3.37 g/cm(3),and relative density was 94.1%. With 1 wt% ZrO2 , the bulk densities of magnesia prepared from crystalline bischofite and brine were 3.10 and 3.27 g/cm(3), and the relative densities increased by 10.0% and 19.6%, respectively. The main reasons for promoting MgO sintering with ZrO2 were that monoclinic phase ZrO2 converted to cubic phase ZrO2 and excess ZrO2 reacted with MgO to generate Mg0.13Zr0.87O1.87, which activated lattice and promoted the diffusion of ions during sintering process. In addition, liquid phase sintering was also one of the main reasons for promoting the sintering of brine magnesia.