Study on microstructure and high temperature oxidation resistance of laser cladding coating prepared by Ni60-TiO2-B4C-Al powders

被引：0
|
作者：
Zhou Fang [1 ]
Yang Huiyao [1 ]
He Lianghua [1 ]
机构：
[1] Guizhou Univ, Sch Met & Mat, Guiyang 550025, Guizhou, Peoples R China
来源：
MATERIALS SCIENCE, CIVIL ENGINEERING AND ARCHITECTURE SCIENCE, MECHANICAL ENGINEERING AND MANUFACTURING TECHNOLOGY, PTS 1 AND 2 | 2014年 / 488-489卷
关键词：
laser cladding; coating; microstructure; oxidation resistance; ALLOY; BEHAVIOR;
D O I：
10.4028/www.scientific.net/AMM.488-489.201
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The composite coating with TiC-TiB2-Ni3Al was fabricated on 45 steel by laser cladding. The microstructure and high temperature oxidation resistance of coating were investigated. The results show that, the main phases of coating are alpha-Fe, TiC, TiB2, Ni3Al, (Fe,Cr)(7)C-3 and Al2O3. The interface of coating and substrate material is metallurgical bond; the coating is uniform and dense without cracks and pores. The fine particles of TiC and TiB2 disperse uniformly in the coating. After oxidized at 1000 degrees C for 60 h, the oxidation film is consisted of spherical oxides of Al, Ti and Cr, they can hinder the diffusion between oxygen and metal atoms and make the coating possess outstanding high temperature oxidation resistance.
引用
收藏
页码：201 / 204
页数：4
相关论文
共 50 条
  • [1] Microstructure and wear resistance of composite coating by laser cladding Ni60A/B4C pre-placed powders on Ti-6Al-4V substrate
    Zhang, Hongxia
    Yu, Huijun
    Chen, Chuanzhong
    SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 2017, 24 (04) : 541 - 546
  • [2] Microstructure and Corrosion Resistance of Ni-Al2O3 Composite Coating Prepared by Laser Cladding
    Sun Y.
    Yan H.
    Lan H.
    Huang C.
    Yu S.
    Sun X.
    Zhang W.
    Surface Technology, 2024, 53 (01): : 143 - 152
  • [3] The microstructure and high-temperature oxidation resistance of Si-rich Mo-Si-B coatings prepared by ultrasonic vibration assisted laser cladding
    Jin, Ming
    He, Dingyong
    Shao, Wei
    Tan, Zhen
    Cao, Qing
    Guo, Xingye
    Zhou, Zheng
    Cui, Li
    Zhou, Lian
    JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 953
  • [4] Microstructure and Wear Resistance of a Cr7C3 Reinforced Ni3Al Composite Coating Prepared by Laser Cladding
    Liu, Zhenbo
    Yin, Fuxing
    Chen, Cuixin
    Zhao, Lin
    Fu, Lihua
    Feng, Yingkai
    Cao, Yang
    Peng, Yun
    Tian, Zhiling
    Li, Changhai
    COATINGS, 2022, 12 (01)
  • [5] Microstructure and high temperature oxidation behavior of laser cladding C22 coating
    Kong, Yao
    Liu, Zongde
    Wang, Xinyu
    Li, Jueyan
    Liu, Quanbing
    MATERIALS TODAY COMMUNICATIONS, 2022, 33
  • [6] Microstructure and high-temperature oxidation resistance of in-situ synthesized Ti-Al-Si composite coating by laser cladding
    Wang, Yueyi
    Hao, Xuanhong
    Liu, Yaxia
    Yang, Chen
    Liu, Hongxi
    Zhang, Xiaowei
    PHYSICA SCRIPTA, 2024, 99 (09)
  • [7] Microstructure and high-temperature oxidation resistance of NiCrAlSi composite coating on Ti6Al4V alloy by laser cladding
    Xu J.-N.
    Liu X.-B.
    Qiao S.-J.
    Zhai Y.-J.
    Tu R.
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2018, 28 (01): : 46 - 52
  • [8] Microstructure and high temperature oxidation resistance of Ti-Ni gradient coating on TA2 titanium alloy fabricated by laser cladding
    Liu, Fencheng
    Mao, Yuqing
    Lin, Xin
    Zhou, Baosheng
    Qian, Tao
    OPTICS AND LASER TECHNOLOGY, 2016, 83 : 140 - 147
  • [9] A study on microstructure and flame erosion mechanism of a graded Ni-Cr-B-Si coating prepared by laser cladding
    Xuan, Hui-Feng
    Wang, Qin-Ying
    Bai, Shu-Lin
    Liu, Zong-De
    Sun, Hua-Gang
    Yan, Peng-Cheng
    SURFACE & COATINGS TECHNOLOGY, 2014, 244 : 203 - 209
  • [10] Microstructure and Thermal Physical Parameters of Ni60-Cr3C2 Composite Coating by Laser Cladding
    Pan Chenggang
    Wang Huachang
    Wang Hongfu
    Chang Qingming
    Wang Huajun
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2010, 25 (06): : 991 - 995
12345