Effect of Sizing on the Interfacial Shear Strength of Carbon Fiber/Epoxy Resin Monofilament Composite

被引：14

作者：

Yang Yusong ^{[1
]}

Zhao Yan ^{[1
]}

Li Ye ^{[1
]}

Dong Qi ^{[1
]}

Chen Da ^{[1
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China

来源：

JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2014年 / 29卷 / 03期

关键词：

interface; SFFT; sizing; hydrothermal aging; BEHAVIOR; ENVIRONMENT; FIBERS;

D O I：

10.1007/s11595-014-0944-1

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The single fiber fragmentation test (SFFT) was used to measure the interfacial shear strength (IFSS) of sized and unsized CF800/epoxy resin monofilament composite in order to evaluate the effect of sizing respectively. Besides, the interfacial reinforcing mechanism was explored by analyzing the surface morphology of the carbon fibers, the wettability between the carbon fibers and the epoxy resin, and the chemical characteristics of the fiber surface. Moreover, the effect of sizing on heat and humidity resistance of interface was investigated by aging test. The results show that sizing improves IFSS of CF800/epoxy resin monofilament composite by 59% through increasing the functional groups containing oxygen and through enhancing wettability, while after sizing the heat and humidity resistance of interface is decreased.

引用

页码：483 / 487

页数：5

共 28 条

[11] Experimental testing and phenomenological modelling of the fragmentation process of braided carbon/epoxy composite tubes under axial and oblique impact [J].

Greve, L. ;

Pickett, A. K. ;

Payen, F. .

COMPOSITES PART B-ENGINEERING, 2008, 39 (7-8) :1221-1232

[12] HYDROTHERMAL ENVIRONMENT INFLUENCE ON WATER DIFFUSION AND MECHANICAL-BEHAVIOR OF CARBON-FIBER EPOXY LAMINATES [J].

IMAZ, JJ ;

RODRIGUEZ, JL ;

RUBIO, A ;

MONDRAGON, I .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1991, 10 (11) :662-665

[13] Accelerated hygrothermal cyclical tests for carbon/epoxy laminates [J].

Jedidi, J ;

Jacquemin, F ;

Vautrin, A .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2006, 37 (04) :636-645

[14] Fiber/epoxy interfacial shear strength measured by the microdroplet test [J].

Kang, Soo-Keun ;

Lee, Deok-Bo ;

Choi, Nak-Sam .

COMPOSITES SCIENCE AND TECHNOLOGY, 2009, 69 (02) :245-251

[15] TENSILE PROPERTIES OF FIBRE-REINFORCED METALS - COPPER/TUNGSTEN AND COPPER/MOLYBDENUM [J].

KELLY, A ;

TYSON, WR .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1965, 13 (06) :329-&

[16] STATISTICAL PROPERTIES OF WEIBULL ESTIMATORS [J].

KHALILI, A ;

KROMP, K .

JOURNAL OF MATERIALS SCIENCE, 1991, 26 (24) :6741-6752

[17]

Kislev T, 2002, ADV COMPOS LETT, V11, P7

[18] Surface and wettability property analysis of CCF300 carbon fibers with different sizing or without sizing [J].

Luo, Yunfeng ;

Zhao, Yan ;

Duan, Yuexin ;

Du, Shanyi .

MATERIALS & DESIGN, 2011, 32 (02) :941-946

[19] INTERFACIAL SHEAR-STRENGTH STUDIES USING THE SINGLE-FILAMENT-COMPOSITE TEST .1. EXPERIMENTS ON GRAPHITE FIBERS IN EPOXY [J].

NETRAVALI, AN ;

HENSTENBURG, RB ;

PHOENIX, SL ;

SCHWARTZ, P .

POLYMER COMPOSITES, 1989, 10 (04) :226-241

[20] Micromechanical modeling of the microbond test to quantify the interfacial properties of fiber-reinforced composites [J].

Nishikawa, M. ;

Okabe, T. ;

Hemmi, K. ;

Takeda, N. .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2008, 45 (14-15) :4098-4113

← 1 2 3 →