Microstructure and Property of ZrO2 Joint Direct Brazed with Aluminum

被引：0
|
作者：
Qi, Xiaoben [1 ]
Ma, Bingyang [1 ]
Shang, Hailong [1 ]
Zhang, Rulin [1 ]
Lu, Jingke [1 ]
Fu, Jiabin [1 ]
Xu, Hao [1 ]
机构：
[1] Shanghai Dianji Univ, Sch Mat Engn, Shanghai 201306, Peoples R China
来源：
MATERIALS TRANSACTIONS | 2020年 / 61卷 / 07期
关键词：
ZrO2; ceramic; direct brazing; Al solder; joint strength; WETTABILITY; STRENGTH; METALS; COPPER;
D O I：
10.2320/matertrans.MT-M2020005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to realize direct brazing ZrO2 with Al, a kind of sputtering Ni/Al double layer on Al solder surface was used. Results showed that ZrO2 could directly brazed to Al solder with sputtering Ni/Al double layer without interface reaction. And then direct brazing was investigated with the change of brazing temperature. Microstructure and joint strength of brazing seam were analyzed. Results showed that joint strength of brazing seam increased from 68.6 MPa to 121.2MPa with the increasement of brazing temperature from 680 degrees C to 840 degrees C, when the brazing temperature increased up to 920 degrees C, the joint strength gradually increased to 122.6 MPa. With the joint strength enhancement of brazing seam, the fracture of the joint is gradually transferred from interface to the brazing seam.
引用
收藏
页码：1252 / 1257
页数：6
相关论文
共 50 条
  • [41] Effect of annealing on corrosion property of aluminum/steel dissimilar metal fusion-brazed joint
    Gu Y.
    Ma M.
    Li J.
    Huang J.
    Shi Y.
    1600, Harbin Research Institute of Welding (38): : 46 - 50
  • [42] Microstructure and property of SiC ceramic brazed joint filled with Ti foam/AlSiMg filler metal
    Li J.
    Li L.
    Qin Q.
    Tu Q.
    He P.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2022, 43 (09): : 86 - 91
  • [43] Effect of ZrO2 on Microstructure and Microhardness for Laser Sintered Al2O3/SiO2/ZrO2
    王蔚
    刘永贤
    Fuh Y.X.Jerry
    中国机械工程, 2014, (06) : 727 - 730
  • [44] Effect of heat treatment on property of brazed joint
    Jia, Qianzhong, 1600, Transport and Telecommunication Institute, Lomonosova street 1, Riga, LV-1019, Latvia (18):
  • [45] Microstructure and mechanical property of the ZrB2-based ultra-high-temperature ceramic composites brazed joint
    Li, Zhuoran
    Wu, Guangdong
    Wang, Zhengzheng
    Feng, Jicai
    ADVANCED MANUFACTURING TECHNOLOGY, PTS 1-3, 2011, 314-316 : 1184 - 1188
  • [46] Microstructure and mechanical property of MGH956 superalloy joint brazed with CuMnNiCo filler metal
    Li, Xiao-Qiang
    Ao, Jing-Pei
    Li, Zi-Yang
    Li, Li
    Qu, Sheng-Guan
    Cailiao Gongcheng/Journal of Materials Engineering, 2015, 43 (05): : 21 - 26
  • [47] Microstructure and Property of AlN Joint Brazed with Au–Pd–Co–Ni–V Brazing Filler
    Bo Chen
    Huaping Xiong
    Yaoyong Cheng
    Wei Mao
    Shibiao Wu
    JournalofMaterialsScience&Technology, 2015, 31 (10) : 1034 - 1038
  • [48] Microstructure and Property of Cu/Al Joint Brazed with Al-Si-Ge Filler Metal
    Niu Zhiwei
    Ye Zheng
    Liu Kaikai
    Huang Jihua
    Chen Shuhai
    Zhao Xingke
    ACTA METALLURGICA SINICA, 2017, 53 (06) : 719 - 725
  • [49] Optical property of CdS nanocrystals in ZrO2 thin film
    Li, Dan
    Ma, Guohong
    Huang, Weimin
    Qian, Shixiong
    Guangxue Xuebao/Acta Optica Sinica, 2002, 22 (06): : 688 - 691
  • [50] THE CORRELATION BETWEEN ZrO2 PHASE AND ITS CATALYTIC PROPERTY
    Wen LI
    Xin Mei WANG
    Yuan Qi YIN Lanzhou InStitule of Chemical Physics
    ChineseChemicalLetters, 1995, (01) : 83 - 86
12345