Microstructure and Property of ZrO2 Joint Direct Brazed with Aluminum

被引：0
|
作者：
Qi, Xiaoben [1 ]
Ma, Bingyang [1 ]
Shang, Hailong [1 ]
Zhang, Rulin [1 ]
Lu, Jingke [1 ]
Fu, Jiabin [1 ]
Xu, Hao [1 ]
机构：
[1] Shanghai Dianji Univ, Sch Mat Engn, Shanghai 201306, Peoples R China
来源：
MATERIALS TRANSACTIONS | 2020年 / 61卷 / 07期
关键词：
ZrO2; ceramic; direct brazing; Al solder; joint strength; WETTABILITY; STRENGTH; METALS; COPPER;
D O I：
10.2320/matertrans.MT-M2020005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to realize direct brazing ZrO2 with Al, a kind of sputtering Ni/Al double layer on Al solder surface was used. Results showed that ZrO2 could directly brazed to Al solder with sputtering Ni/Al double layer without interface reaction. And then direct brazing was investigated with the change of brazing temperature. Microstructure and joint strength of brazing seam were analyzed. Results showed that joint strength of brazing seam increased from 68.6 MPa to 121.2MPa with the increasement of brazing temperature from 680 degrees C to 840 degrees C, when the brazing temperature increased up to 920 degrees C, the joint strength gradually increased to 122.6 MPa. With the joint strength enhancement of brazing seam, the fracture of the joint is gradually transferred from interface to the brazing seam.
引用
收藏
页码：1252 / 1257
页数：6
相关论文
共 50 条
  • [21] Microstructure evolution and mechanical properties of ZrO2/TiAl joints vacuum brazed by Ag-Cu filler metal
    Feng, Jicai
    Dai, Xiangyu
    Wang, Dong
    Li, Rui
    Cao, Jian
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 639 : 739 - 746
  • [22] Microstructure Changes of Aluminum Titanate Refractory Doped SiO2 and ZrO2 in Molten Steel
    Kim, Dann
    Kim, Hyung-Tae
    Ryu, Sung-Soo
    Kim, Hyeong-Jun
    KOREAN JOURNAL OF METALS AND MATERIALS, 2015, 53 (02): : 116 - 122
  • [23] Preparation and thermodynamic analysis of the porous ZrO2/(ZrO2 + Ni) functionally graded bolted joint
    Zhou, Wenbin
    Ai, Shigang
    Chen, Mingji
    Zhang, Rubing
    He, Rujie
    Pei, Yongmao
    Fang, Daining
    COMPOSITES PART B-ENGINEERING, 2015, 82 : 13 - 22
  • [24] Effect of AlN and ZrO2 on the microstructure and property of the 2Si-B-3C-N ceramic
    Zhang, Pengfei
    Yang, Bin
    Lu, Zhi
    Jia, Dechang
    CERAMICS INTERNATIONAL, 2018, 44 (03) : 3406 - 3411
  • [25] Effect of holding time on microstructure and mechanical properties of ZrO2/TiAl joints brazed by Ag-Cu filler metal
    Dai, Xiangyu
    Cao, Jian
    Liu, Jiakun
    Su, Shuai
    Feng, Jicai
    MATERIALS & DESIGN, 2015, 87 : 53 - 59
  • [26] Microstructure-mechanical-tribological property correlation of multistage spark plasma sintered tetragonal ZrO2
    Reddy, K. Madhav
    Mukhopadhyay, Amartya
    Basu, Bikramjit
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2010, 30 (16) : 3363 - 3375
  • [27] MICROSTRUCTURE OF MULLITE/ZRO2 AND MULLITE/AL2O3/ZRO2 TOUGH CERAMIC COMPOSITES
    RINCON, JM
    DINGER, TR
    THOMAS, G
    MOYA, JS
    OSENDI, MI
    ACTA METALLURGICA, 1987, 35 (05): : 1175 - 1179
  • [28] Microstructure and thermal conductivity of porous ZrO2 ceramics
    Deng, Zhen-Yan
    Ferreira, Jose M. F.
    Tanaka, Yoshihisa
    Isoda, Yukihiro
    ACTA MATERIALIA, 2007, 55 (11) : 3663 - 3669
  • [29] Effect of ZrO2 additions on the microstructure, mechanical and wear properties of ZrO2/7075 aluminium alloy composite
    Zhang, Ji-dong
    Zhang, Lan
    Ma, Hui-zhong
    MATERIALS TODAY COMMUNICATIONS, 2023, 37
  • [30] The microstructure of Ni/ZrO2 infiltrated composite layer
    Sun, Xian-ming
    Li, Jian
    Yan, Gui-rong
    Song, Wen-ming
    Ma, Ying
    ADVANCED MANUFACTURING TECHNOLOGY, PTS 1-3, 2011, 314-316 : 236 - +
12345