Microstructure and Property of ZrO2 Joint Direct Brazed with Aluminum

被引：0
|
作者：
Qi, Xiaoben [1 ]
Ma, Bingyang [1 ]
Shang, Hailong [1 ]
Zhang, Rulin [1 ]
Lu, Jingke [1 ]
Fu, Jiabin [1 ]
Xu, Hao [1 ]
机构：
[1] Shanghai Dianji Univ, Sch Mat Engn, Shanghai 201306, Peoples R China
来源：
MATERIALS TRANSACTIONS | 2020年 / 61卷 / 07期
关键词：
ZrO2; ceramic; direct brazing; Al solder; joint strength; WETTABILITY; STRENGTH; METALS; COPPER;
D O I：
10.2320/matertrans.MT-M2020005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to realize direct brazing ZrO2 with Al, a kind of sputtering Ni/Al double layer on Al solder surface was used. Results showed that ZrO2 could directly brazed to Al solder with sputtering Ni/Al double layer without interface reaction. And then direct brazing was investigated with the change of brazing temperature. Microstructure and joint strength of brazing seam were analyzed. Results showed that joint strength of brazing seam increased from 68.6 MPa to 121.2MPa with the increasement of brazing temperature from 680 degrees C to 840 degrees C, when the brazing temperature increased up to 920 degrees C, the joint strength gradually increased to 122.6 MPa. With the joint strength enhancement of brazing seam, the fracture of the joint is gradually transferred from interface to the brazing seam.
引用
收藏
页码：1252 / 1257
页数：6
相关论文
共 50 条
  • [1] Interfacial Microstructure and Mechanical Property of ZrO2 Joints Brazed with Ni-Ti Filler Metal
    Zhang Q.
    Wang J.
    Zheng K.
    Yang H.
    Wang, Juan (sweetanna@foxmail.com), 1600, Chinese Ceramic Society (48): : 1430 - 1436
  • [2] Evaluation of Biomedical Ti/ZrO2 Joint Brazed with Pure Au Filler: Microstructure and Mechanical Properties
    Lei, Yuzhen
    Bian, Hong
    Fu, Wei
    Song, Xiaoguo
    Feng, Jicai
    Long, Weimin
    Niu, Hongwei
    METALS, 2020, 10 (04)
  • [3] Microstructure evolution and mechanical properties of ZrO2/ZrO2 joints brazed with Ni?Ti filler metal
    Zhang, Qi
    Wang, Juan
    Zheng, Kaihong
    Lu, Yao
    Yang, Hongwang
    MATERIALS RESEARCH EXPRESS, 2019, 6 (12)
  • [4] MICROSTRUCTURE AND RESISTING LASER DAMAGE PROPERTY OF ZrO2 FILMS
    Liu An-Ping
    Han Wei-Feng
    Huang Mao
    Luo Qing-Chun
    JOURNAL OF INFRARED AND MILLIMETER WAVES, 2010, 29 (05) : 333 - +
  • [5] Microstructure of ZrO2 nanoceramics
    Karban, O. V.
    Khasanov, O. L.
    Kanunnikova, O. M.
    JOURNAL OF STRUCTURAL CHEMISTRY, 2004, 45 (Suppl 1) : S147 - S153
  • [6] Microstructure of ZrO2 nanoceramics
    O. V. Karban
    O. L. Khasanov
    O. M. Kanunnikova
    Journal of Structural Chemistry, 2004, 45 : S147 - S153
  • [7] Interfacial microstructure and mechanical property of brazed copper/SiO2 ceramic joint
    Song, Y. Y.
    Li, H. L.
    Zhao, H. Y.
    Liu, D.
    Song, X. G.
    Feng, J. C.
    VACUUM, 2017, 141 : 116 - 123
  • [8] Effect of ZrO2 content on the mechanical properties and microstructure of HAp/ZrO2 nanocomposites
    Kumar, V. Ajay
    Raju, P. Rama Murty
    Ramanaiah, N.
    Siriyala, Rajesh
    CERAMICS INTERNATIONAL, 2018, 44 (09) : 10345 - 10351
  • [9] Investigation of microstructure and properties near the interface of copper/aluminum brazed joint
    Xia, C. Z.
    Liang, Q. H.
    Chen, D. F.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2013, 51 (04): : 235 - 239
  • [10] Interfacial Microstructure and Mechanical Properties of Reactive Air Brazed Joints of ZrO2 Ceramic and GH3536
    Yang Junhao
    Yang Zhenwen
    Wang Ying
    Song Kuijing
    Wang Dongpo
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (12) : 4450 - 4456
12345