Hydrothermal synthesis and characterization of copper containing crystalline silicate mesoporous materials from gel mixture

被引：10

作者：

Chatterjee, M ^{[1
]}

Iwasaki, T ^{[1
]}

Onodera, Y ^{[1
]}

Hayashi, H ^{[1
]}

Ikushima, Y ^{[1
]}

Nagase, T ^{[1
]}

Ebina, T ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Supercrit Fluid Res Ctr, Miyagino Ku, Sendai, Miyagi 9838551, Japan

来源：

APPLIED CLAY SCIENCE | 2004年 / 25卷 / 3-4期

关键词：

Cu-SCMM; characterization; ESR; supercritical carbon dioxide; selective hydrogenation;

D O I：

10.1016/j.clay.2003.11.003

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Novel copper-containing crystalline silicate mesoporous materials (SCMM) have been synthesized by the hydrothermal treatment of slurries of silicon-magnesium-copper hydroxide precipitates along with quaternary ammonium salt. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed a house-of-cards type structure consists of very thin platy silicates. Nitrogen adsorption-desorption isotherms of calcined material show that it has a high surface area (similar to 550 m(2) g(-1)) and porosity properties. Pore characteristics are similar to that of MCM-41 and FSM-16, and fine-tuning of the pore size was achieved easily by modulating the synthesis temperature. Identification and the location of copper species in Cu-SCMM were done by X-ray photoelectron spectroscopy (XPS) and electron spin resonance (ESR), respectively. ESR data of air-dried Cu-SCMM consist of clearly defined g(\\) = 2.34, A(\\) = 140 x 10(-4) cm(-1) and g(perpendicular to) = 2.08 at room temperature and g(parallel to) = 2.34, A(parallel to) = 160 x 10(-4) cm(-1) and g(perpendicular to) = 2.10 at 77 K. The resulting material exhibited superior catalytic activity towards the hydrogenation of alpha-beta unsaturated aldehyde in supercritical carbon dioxide. (C) 2003 Elsevier B.V. All rights reserved.

引用

页码：195 / 205

页数：11

共 34 条

[1] A NEW FAMILY OF MESOPOROUS MOLECULAR-SIEVES PREPARED WITH LIQUID-CRYSTAL TEMPLATES
BECK, JS
VARTULI, JC
ROTH, WJ
LEONOWICZ, ME
KRESGE, CT
SCHMITT, KD
CHU, CTW
OLSON, DH
SHEPPARD, EW
MCCULLEN, SB
HIGGINS, JB
SCHLENKER, JL
[J]. JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1992, 114 (27) : 10834 - 10843
[2] SYNTHESIS OF ALUMINUM-RICH MCM-41
BORADE, RB
CLEARFIELD, A
[J]. CATALYSIS LETTERS, 1995, 31 (2-3) : 267 - 272
[3] STEREOCHEMISTRY OF HYDRATED COPPER(II) IONS ON INTERLAMELLAR SURFACES OF LAYER SILICATES - ELECTRON-SPIN RESONANCE STUDY
CLEMENTZ, DM
PINNAVAIA, TJ
MORTLAND, MM
[J]. JOURNAL OF PHYSICAL CHEMISTRY, 1973, 77 (02) : 196 - 200
[4] COORDINATION OF CUPRIC IONS TO WATER AND TO METAL-OXIDE PILLARS IN COPPER(II)-DOPED, AL-13-PILLARED AND ZR-4-PILLARED MONTMORILLONITE CLAYS STUDIED BY ELECTRON-SPIN ECHO MODULATION SPECTROSCOPY
COMETS, JM
KEVAN, L
[J]. JOURNAL OF PHYSICAL CHEMISTRY, 1993, 97 (46) : 12004 - 12007
[5] Determining the nature of the active sites of Cu-beta zeolites for the selective catalytic reduction (SGR) of NOx by using a coupled reaction XAES/XPS study
Corma, A
Palomares, A
Marquez, F
[J]. JOURNAL OF CATALYSIS, 1997, 170 (01) : 132 - 139
[6] Selective catalytic reduction of NOx on Cu-beta zeolites
Corma, A
Fornes, V
Palomares, E
[J]. APPLIED CATALYSIS B-ENVIRONMENTAL, 1997, 11 (02) : 233 - 242
[7] DEBOER JH, 1957, STRUCTURE PROPERTIES
[8] Adsorption of Cu(II) on the (0001) plane of mica: A REFLEXAFS and XPS study
Farquhar, ML
Charnock, JM
England, KER
Vaughan, DJ
[J]. JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1996, 177 (02) : 561 - 567
[9] HARUO S, 1988, NENDO KOBUTSUGAKU, P74
[10] HELD W, 1987, Patent No. 3642018

← 1 2 3 4 →