Angular distortion of fillet welded T joint using low transformation temperature welding wire

被引:55
作者
Mikami, Y. [1 ]
Morikage, Y.
Mochizuki, M. [1 ]
Toyoda, M. [1 ]
机构
[1] Osaka Univ, Grad Sch Engn, Div Mat & Mfg Sci, Suita, Osaka 5650871, Japan
关键词
Low transformation temperature welding wire; Martensitic transformation; Transformation expansion; Finite element method; Numerical simulation; Angular distortion; STEELS; MODEL;
D O I
10.1179/136217108X382972
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A newly developed low transformation temperature welding wire, of which the transformation start temperature is lower than that of conventional welding wires, was applied to fabrication of fillet welded T joints. The welding angular distortion and the temperature profile of the weld metal were continuously measured during the welding process. The angular distortion of the fabricated T joint was reduced when the weld metal reached the martensitic transformation start temperature. The residual angular distortion was less with the low transformation temperature welding wire than that with the conventional welding wires. The welding distortion of T joints was calculated by a numerical simulation with consideration of the effect of phase transformation under weld thermal cycles. The welding distortion was reproduced with high accuracy in the numerical simulation. Results of the numerical simulation also determined that there was a direct correspondence between the transformation expansion of the weld metal and the angular distortion.
引用
收藏
页码:97 / 105
页数:9
相关论文
共 20 条
[1]  
[Anonymous], P C RES STRESS WELD
[2]   Developments in martensitic and bainitic steels: role of the shape deformation [J].
Bhadeshia, HKDH .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 378 (1-2) :34-39
[3]   Fatigue properties of longitudinal attachments welded using low transformation temperature filler [J].
Eckerlid, J ;
Nilsson, T ;
Karlsson, L .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2003, 8 (05) :353-359
[4]  
*ESI GROUP, 2004, SYSWELD REF MAN
[5]  
FRANCIS JA, 2007, P ASME PVP C SAN ANT
[6]  
Guan Q., 1994, WELD WORLD, V33, P160
[7]   A GENERAL EQUATION PRESCRIBING THE EXTENT OF THE AUSTENITE-MARTENSITE TRANSFORMATION IN PURE IRON-CARBON ALLOYS AND PLAIN CARBON STEELS [J].
KOISTINEN, DP ;
MARBURGER, RE .
ACTA METALLURGICA, 1959, 7 (01) :59-60
[8]   A NEW KINETIC-MODEL FOR ANISOTHERMAL METALLURGICAL TRANSFORMATIONS IN STEELS INCLUDING EFFECT OF AUSTENITE GRAIN-SIZE [J].
LEBLOND, JB ;
DEVAUX, J .
ACTA METALLURGICA, 1984, 32 (01) :137-146
[9]  
Mochizuki M, 2006, WELD WORLD, V50, P46
[10]  
Murakawa H., 1996, TRANSACTION JOINING, V25, P191