Study of laser MIG hybrid welded AZ31 magnesium alloy

被引：51

作者：

Gao, M. ^{[1
]}

Zeng, X. Y. ^{[1
]}

Tan, B. ^{[2
]}

Feng, J. C. ^{[2
]}

机构：

[1] Huazhong Univ Sci & Technol, Wuhan Natl Lab Optoelect, Wuhan 430074, Peoples R China

[2] China Acad Ordnance Sci, Ningbo Branch, Ningbo 315103, Zhejiang, Peoples R China

来源：

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2009年 / 14卷 / 04期

基金：

中国博士后科学基金;

关键词：

Hybrid welding; Magnesium alloys; Weld shape; Microstructure; Tensile properties; TUNGSTEN INERT-GAS; MECHANICAL-PROPERTIES; WELDING BEHAVIOR; PORE FORMATION; BEAM; MICROSTRUCTURE; PARAMETERS; CO2; SHAPE;

D O I：

10.1179/136217109X406929

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The laser metal inert gas (MIG) hybrid welded AZ31 magnesium alloy is discussed in weld shape, microstructure characteristics and mechanical properties in comparison of single laser and arc welding. The stable MIG arc, reliable droplet transfer and regular weld that are hardly obtained in single MIG welding can be obtained in hybrid welding by laser arc synergic effects. The ultimate tensile strength and elongation of hybrid weld are far higher than those of laser weld and reach 97.8 and 87.5% of base metal respectively. Under this experimental condition, the efficiency of hybrid welding is 1.20 times faster than that of single laser welding. Between the wide upper part (arc zone) and the narrow lower part (laser zone), obvious difference is observed. Arc zone has coarser grain size and wider partial melted zone than laser zone. Finally, the porosity reduction mechanism of hybrid weld is discussed according to the weld pool shape and the acting forces on it.

引用

页码：274 / 281

页数：8

共 39 条

[1]

[Anonymous], P 23 INT C APPL LAS

[2]

[Anonymous], 2002, WELDING METALLURGY

[3] Review of laser hybrid welding [J].

Bagger, C ;

Olsen, FO .

JOURNAL OF LASER APPLICATIONS, 2005, 17 (01) :2-14

[4] A review of laser welding techniques for magnesium alloys [J].

Cao, X ;

Jahazi, M ;

Immarigeon, JP ;

Wallace, W .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 171 (02) :188-204

[5] Statistical analysis of MIG-laser CO2 hybrid welding of Al-Mg alloy [J].

Casalino, G. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 191 (1-3) :106-110

[6] Optimal parameters for low and high voltage electron beam welding of AZ series magnesium alloys and mechanism of weld shape and pore formation [J].

Chi, C. -T. ;

Chao, C. -G. ;

Liu, T. -F. ;

Wang, C. -C. .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2008, 13 (02) :199-211

[7] Aluminum element effect for electron beam welding of similar and dissimilar magnesium-aluminum-zinc alloys [J].

Chi, Chao-Ting ;

Chao, Chuen-Guang ;

Liu, Tzeng-Feng ;

Lee, Chuan-Hua .

SCRIPTA MATERIALIA, 2007, 56 (09) :733-736

[8] Microstructure and mechanical properties of magnesium alloy AZ31B laser beam welds [J].

Coelho, R. S. ;

Kostka, A. ;

Pinto, H. ;

Riekehr, S. ;

Kocak, M. ;

Pyzalla, A. R. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 485 (1-2) :20-30

[9] Interaction of the keyhole and weld pool in laser keyhole welding [J].

Dowden, J .

JOURNAL OF LASER APPLICATIONS, 2002, 14 (04) :204-209

[10] Nugget growth characteristic for AZ31B magnesium alloy during resistance spot welding [J].

Feng, JC ;

Wang, YR ;

Zhang, ZD .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2006, 11 (02) :154-162

← 1 2 3 4 →