The effect of nanoparticles on the adhesion of epoxy adhesive

被引：134
作者：
Zhai, Lanlan
Ling, Guoping [1 ]
Li, Jian
Wang, Youwen
机构：
[1] Zhejiang Univ, Coll Mat Sci & Chem Engn, Hangzhou 310027, Peoples R China
[2] Zhejiang Univ, Ctr Anal & Measurement, Hangzhou 310027, Peoples R China
来源：
MATERIALS LETTERS | 2006年 / 60卷 / 25-26期
基金：
中国国家自然科学基金;
关键词：
adhesion; epoxy adhesive; steel substrate; nanoparticles; surface;
D O I：
10.1016/j.matlet.2006.02.038
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this investigation, the influence of different nanoparticles and surface roughness on the adhesion between epoxy adhesive and steel substrate was primarily investigated. The results of pull-off adhesion tests indicated that namo-Al2O3 of the three kinds of nanoparticles had the most influence on adhesion strength, which was the optimal additive for the epoxy adhesive to improve the adhesion strength. Also, it was found that modified by 2% namo-Al2O3, the strength multiplication on the surface abraded with silicon carbide paper of 150 grits (150#) was the highest, of three different surface roughness. So, as the results showed that modified by 2% namo-Al2O3, the adhesion strength of epoxy adhesive on the surface abraded with 150# was visibly improved by about 5 times. Transmission electron microscope (TEM) displayed namo-Al2O3 homogeneously dispersed in epoxy adhesive. Field emission scanning electronic microscope (FE-SEM) revealed that the surface morphology of steel well coincided with that of epoxy adhesive. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：3031 / 3033
页数：3
相关论文
共 14 条
[1]   Studies on thermal and mechanical properties of polyimide-clay nanocomposites [J].
Agag, T ;
Koga, T ;
Takeichi, T .
POLYMER, 2001, 42 (08) :3399-3408
[2]   Suppression of crystal nucleation in polydisperse colloids due to increase of the surface free energy [J].
Auer, S ;
Frenkel, D .
NATURE, 2001, 413 (6857) :711-713
[3]   Effects of titania content and plasma treatment on the interfacial adhesion mechanism of nano titania-hybridized polyimide and copper system [J].
Chiang, PC ;
Whang, WT ;
Wu, SC ;
Chuang, KR .
POLYMER, 2004, 45 (13) :4465-4472
[4]   Preparation of soluble polyimide-silver nanocomposites by a convenient ultraviolet irradiation technique [J].
Huang, JC ;
Qian, XF ;
Yin, J ;
Zhu, ZK ;
Xu, HJ .
MATERIALS CHEMISTRY AND PHYSICS, 2001, 69 (1-3) :172-175
[5]  
Janota R.B., 1983, HIGH PERFORMANCE ADH, P4
[6]  
Kinloch A.J., 1987, ADHESION ADHESIVES S, P3
[7]   Adhesion of epoxy to hydrotalcite conversion coatings: II. Surface modification with ionic surfactants [J].
Leggat, RB ;
Taylor, SA ;
Taylor, SR .
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2002, 210 (01) :83-94
[8]   Nanophases in polymers [J].
Reynaud, E ;
Gauthier, C ;
Perez, J .
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1999, 96 (02) :169-176
[9]   Studies on the tribological behavior and transfer film-counterface bond strength for polyphenylene sulfide filled with nanoscale alumina particles [J].
Schwartz, CJ ;
Bahadur, S .
WEAR, 2000, 237 (02) :261-273
[10]   IEEE Nano 2001 - Nanoscientists look to the future [J].
Service, RF .
SCIENCE, 2001, 294 (5546) :1448-1449
12