TEM study of internal oxidation in an ODS-Eurofer alloy

被引：13

作者：

Klimenkov, M. ^{[1
]}

Lindau, R. ^{[1
]}

Moeslang, A. ^{[1
]}

机构：

[1] Forschungszentrum Karlsruhe, Inst Mat Res 1, D-76344 Eggenstein Leopoldshafen, Germany

来源：

JOURNAL OF NUCLEAR MATERIALS | 2009年 / 386-88卷

关键词：

STEEL;

D O I：

10.1016/j.jnucmat.2008.12.176

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Analytical TEM investigations of samples from an oxide dispersion-strengthened Eurofer batch show the formation of new type of precipitates of Fe-Cr-V-O composition and a size of 40-250 nm. Structural HRTEM analysis reveals that the precipitates consist of (Mn,Fe)(Cr,V)(2)O(4) manganese chromium oxide of spinel structure. In some cases, the inclusions order along lines that can reach more than ten micrometers in length. Such lines of large particles might have a negative influence on the mechanical properties of the steel, as was observed. It is assumed that they form by internal oxidation during hot isostatic pressing due to the high oxygen content of the mechanically alloyed powder. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：557 / 560

页数：4

共 5 条

[1] Oxygen K-edge in vanadium oxides:: simulations and experiments [J].

Hébert, C ;

Willinger, M ;

Su, DS ;

Pongratz, P ;

Schattschneider, P ;

Schlögl, R .

EUROPEAN PHYSICAL JOURNAL B, 2002, 28 (04) :407-414

[2] Direct correlation between morphology of (Fe,Cr)23C6precipitates and impact behavior of ODS steels [J].

Klimiankou, M. ;

Lindau, R. ;

Moeslang, A. .

JOURNAL OF NUCLEAR MATERIALS, 2007, 367 :173-178

[3] TEM study of PM 2000 steel [J].

Klimiankou, M ;

Lindau, R ;

Möslang, A ;

Schröder, J .

POWDER METALLURGY, 2005, 48 (03) :277-287

[4] Mechanical and microstructural properties of a hipped RAFM ODS-steel [J].

Lindau, R ;

Möslang, A ;

Schirra, M ;

Schlossmacher, P ;

Klimenkov, M .

JOURNAL OF NUCLEAR MATERIALS, 2002, 307 (1 SUPPL.) :769-772

[5]

Lindau R., 2005, P 16 INT PLANSEE SEM, V1, P545

← 1 →