Creep rupture of alloy 718 after thermal aging

被引:6
作者
Korth, GE [1 ]
机构
[1] Bechtel BWXT Idaho LLC, Idaho Natl Engn & Environm Lab, Idaho Falls, ID 83415 USA
来源
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY | 2000年 / 52卷 / 01期
关键词
Thermal Aging; Thermal Exposure; Aged Material; Rupture Life; Creep Rupture;
D O I
10.1007/s11837-000-0114-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Alloy 718 given the conventional 718/621 degrees C age-hardening treatment was thermally aged at 593 degrees C, 621 degrees C, nod 649 degrees C for up to 50,000 h. These temperatures bracket Nle lowest of lire duplex age-hardening temperatures. Subsequent creep-rupture tests conducted at the same temperature thermal aging show no detrimental effects of 593 degrees C aging after 50,000 h. Material aged for 50,000 h and tested at 621 degrees C shows the rupture life to be approximately 60-65% of the unaged material, but at 649 degrees C, the aged material rupture life is on the order of 15% of the unaged material.
引用
收藏
页码:40 / +
页数:3
相关论文
共 9 条
[1]  
BARKER JF, 1970, JOM-J MIN MET MAT S, V22, P31
[2]  
Brinkman C, 1991, SUPERALLOYS 718625 V, P519
[3]  
Brooks J. W., 1988, SUPERALLOYS 1988, P33
[4]  
KORTH G, 1983, EGG2229
[5]  
KORTH GE, 1991, SUPERALLOYS 718 625, P437
[6]  
RADAVICH JF, 1992, SUPERALLOYS 1992, P497
[7]  
RADAVICH JF, 1991, SUPERALLOY 718 625 V, P865
[8]  
Radavich JF, 1989, Superalloy 718-Metallurgy and Applications
[9]  
SMOLIK GR, 1978, TREE1253 EG G DOE