Dynamic Response of CoSb2O6 Trirutile-Type Oxides in a CO2 Atmosphere at Low-Temperatures

Experimental work on the synthesis of the CoSb2O6 oxide and its CO2 sensing properties is presented here. The oxide was synthesized by a microwave-assisted colloidal method in presence of ethylenediamine after calcination at 600 degrees C. This CoSb2O6 oxide crystallized in a tetragonal structure with cell parameters a = 4.6495 and c = 9.2763 angstrom, and space group P4(2)/mnm. To prove its physical, chemical and sensing properties, the oxide was subjected to a series of tests: Raman spectroscopy, Scanning Electron Microscopy (SEM) and impedance (Z) measurements. Microstructures, like columns, bars and hollow hemispheres, were observed. For the CO2 sensing test, a thick film of CoSb2O6 was used, measuring the impedance variations on the presence of air/CO2 flows (0.100 sccm/0.100 sccm) using AC (alternating current) signals in the frequency-range 0.1-100 kHz and low relative temperatures (250 and 300 degrees C). The CO2 sensing results were quite good.