Fatigue of steam turbine blades with damage on the leading edge

被引：18

作者：

Shlyannikov, V. N. ^{[1
]}

Yarullin, R. R. ^{[1
]}

Zakharov, A. P. ^{[1
]}

机构：

[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia

来源：

20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷

基金：

俄罗斯基础研究基金会;

关键词：

elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;

D O I：

10.1016/j.mspro.2014.06.289

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.

引用

页码：1792 / 1797

页数：6

共 50 条

[41] Synthetical numerical model for evaluating blade fatigue life of liquid corrosion in steam turbine
Xie, Yonghui
Zhang, Di
Feng, Zhenping
Sun, Bi
FRACTURE AND DAMAGE MECHANICS V, PTS 1 AND 2, 2006, 324-325 : 165 - +
[42] Simulation of residual stress in welded steam turbine rotor and its effects on fatigue life
Feng, Lei
Liu, Xia
Xuan, Fuzhen
Zhongguo Dianji Gongcheng Xuebao/Proceedings of the Chinese Society of Electrical Engineering, 2014, 34 (17): : 2851 - 2860
[43] NANOSTRUCTURED CVD W/WC COATING PROTECTS STEAM AND GAS TURBINE BLADES AGAINST WATER DROPLET EROSION
Zhuk, Yuri
PROCEEDINGS OF ASME TURBO EXPO 2022: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, GT2022, VOL 7, 2022,
[44] Fatigue Life of Megawatt-Scale Composite Wind Turbine Blades with Shallow-Angled Laminates
K. Hayat
S. K. Ha
T. Sultan
Z. Ahmad
Mechanics of Composite Materials, 2019, 55 : 483 - 494
[45] Fatigue Life of Megawatt-Scale Composite Wind Turbine Blades with Shallow-Angled Laminates
Hayat, K.
Ha, S. K.
Sultan, T.
Ahmad, Z.
MECHANICS OF COMPOSITE MATERIALS, 2019, 55 (04) : 483 - 494
[46] MICROSTRUCTURAL ANALYSIS OF GAS TURBINE BLADES
Alomairi, Bassam S.
Driss, Zied
Hashim, Fadel A.
Hussein, Hussein Ali
JOURNAL OF MATERIALS EDUCATION, 2023, 45 (3-6)
[47] Influence of the level of damage on the high temperature fatigue life of an aircraft turbine disc
Silveira, E.
Atxaga, G.
Irisarri, A. M.
ENGINEERING FAILURE ANALYSIS, 2009, 16 (02) : 578 - 584
[48] Effects of shallow angle on static strength and fatigue life of multi-directional laminates for wind turbine blades
Ha, Sung Kyu
Gorostidi Martinez de Lece, Alvaro
Donazar Moriones, Carlos
Cimini Junior, Carlos Alberto
Jin, Chengzhu
JOURNAL OF COMPOSITE MATERIALS, 2017, 51 (18) : 2549 - 2563
[49] Research and engineering application of DED laser cladding repair for steam turbine XM-25 alloy LP blades
Wu, Haitao
An, Tiancheng
Sun, Baihui
Ye, Chuying
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2025,
[50] Fatigue life expenditure assessment and countermeasure for turbine blades due to harmonic excitations of slip energy recovery drives
Tsai, Jong-Ian
EUROPEAN TRANSACTIONS ON ELECTRICAL POWER, 2009, 19 (08): : 1065 - 1081

← 1 2 3 4 5 →