Fatigue of steam turbine blades with damage on the leading edge

被引：18

作者：

Shlyannikov, V. N. ^{[1
]}

Yarullin, R. R. ^{[1
]}

Zakharov, A. P. ^{[1
]}

机构：

[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia

来源：

20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷

基金：

俄罗斯基础研究基金会;

关键词：

elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;

D O I：

10.1016/j.mspro.2014.06.289

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.

引用

页码：1792 / 1797

页数：6

共 50 条

[21] A framework for fatigue reliability analysis of high-pressure turbine blades
Jie Zhou
Hong-Zhong Huang
Yan-Feng Li
Junyu Guo
Annals of Operations Research, 2022, 311 : 489 - 505
[22] A framework for fatigue reliability analysis of high-pressure turbine blades
Zhou, Jie
Huang, Hong-Zhong
Li, Yan-Feng
Guo, Junyu
ANNALS OF OPERATIONS RESEARCH, 2022, 311 (01) : 489 - 505
[23] Forging of Steam Turbine Blades With an Fe3Al-Based Alloy
Janschek, P.
Bauer-Partenheimer, K.
Krein, R.
Hanus, P.
Palm, M.
ADVANCED INTERMETALLIC-BASED ALLOYS FOR EXTREME ENVIRONMENT AND ENERGY APPLICATIONS, 2009, 1128 : 47 - +
[24] REDUCTION OF FATIGUE DAMAGE EQUIVALENT LOADS IN THE WIND TURBINE SYSTEM THROUGH THE USE OF OFF-AXIS PLIES IN THE SPAR CAPS OF COMPOSITE WIND TURBINE BLADES
Gozcu, M. Ozan
Farsadi, Touraj
Sener, Ozgun
Kayran, Altan
20TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS, 2015,
[25] Study of damage and repair of blades of a 300kW wind turbine
Marin, J. C.
Barroso, A.
Paris, F.
Canas, J.
ENERGY, 2008, 33 (07) : 1068 - 1083
[26] Microstructural Damage Analysis of Service Turbine Blades for an Aero-engine
Fan Y.
Huang W.
Yang X.
Shi D.
Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2019, 55 (13): : 122 - 128
[27] Calculation and enhancement of fatigue life by ε-N approach and corrosion fatigue in steam turbine rotor
Silva, Jose Antonio
Caetano, Diego Amorim
Moni Ribeiro Filho, Sergio Luiz
Teixeira, Flavio Neves
Monteiro Guimaraes, Luiz Gustavo
INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2022, 31 (06) : 845 - 863
[28] COMPUTER SIMULATION OF FATIGUE, CREEP AND THERMAL-FATIGUE CRACKS PROPAGATION IN GAS-TURBINE BLADES
Semenov, Artem
Semenov, Sergey
Nazarenko, Anatoly
Getsov, Leonid
MATERIALI IN TEHNOLOGIJE, 2012, 46 (03): : 197 - 203
[29] Fatigue failure in high-temperature single crystal superalloy turbine blades
Arakere, NK
Moroso, J
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2001, 20 (02) : 117 - 135
[30] THERMO-MECHANICAL FATIGUE EXPERIMENTS OF SINGLE CRYSTAL HOLLOW TURBINE BLADES
Jing, Fulei
Wang, Rongqiao
Hu, Dianyin
PROCEEDINGS OF THE ASME TURBO EXPO 2012, VOL 7, PTS A AND B, 2012, : 143 - +

← 1 2 3 4 5 →