Fatigue of steam turbine blades with damage on the leading edge

被引：18
|
作者：
Shlyannikov, V. N. [1 ]
Yarullin, R. R. [1 ]
Zakharov, A. P. [1 ]
机构：
[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia
来源：
20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷
基金：
俄罗斯基础研究基金会;
关键词：
elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;
D O I：
10.1016/j.mspro.2014.06.289
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.
引用
收藏
页码：1792 / 1797
页数：6
相关论文
共 50 条
  • [1] Study of fatigue damage in wind turbine blades
    Marin, J. C.
    Barroso, A.
    Paris, F.
    Canas, J.
    ENGINEERING FAILURE ANALYSIS, 2009, 16 (02) : 656 - 668
  • [2] On erosion issues associated with the leading edge of wind turbine blades
    Keegan, M. H.
    Nash, D. H.
    Stack, M. M.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2013, 46 (38)
  • [3] Fatigue damage prevention on turbine blades: study of underplatform damper shape
    Berruti, T.
    Firrone, C. M.
    Pizzolante, M.
    Gola, M. M.
    DAMAGE ASSESSMENT OF STRUCTURES VII, 2007, 347 : 159 - +
  • [4] Nanoengineered Graphene-Reinforced Coating for Leading Edge Protection of Wind Turbine Blades
    Johansen, Nicolai Frost-Jensen
    Mishnaevsky, Leon, Jr.
    Dashtkar, Arash
    Williams, Neil A.
    Faester, Soren
    Silvello, Alessio
    Cano, Irene Garcia
    Hadavinia, Homayoun
    COATINGS, 2021, 11 (09)
  • [5] Shot-Peening of Steam Turbine Blades: Residual Stresses and their Modification by Fatigue Cycling
    James, M. N.
    Newby, M.
    Hattingh, D. G.
    Steuwer, A.
    FATIGUE 2010, 2010, 2 (01): : 441 - 451
  • [6] Leading edge erosion of coated wind turbine blades: Review of coating life models
    Slot, H. M.
    Gelinck, E. R. M.
    Rentrop, C.
    van der Heide, E.
    RENEWABLE ENERGY, 2015, 80 : 837 - 848
  • [7] Fatigue Fracture of Turbine Blades: Case Studies
    Kianicova, Marta
    Pokluda, Jaroslav
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE VII, 2014, 592-593 : 712 - 715
  • [8] An investigation of the failure of low pressure steam turbine blades
    Wang, WZ
    Xuan, FZ
    Zhu, KL
    Tu, ST
    MULTISCALE DAMAGE RELATED TO ENVIRONMENT ASSISTED CRACKING, 2005, : 229 - 234
  • [9] Threshold damage-based fatigue life prediction of turbine blades under combined high and low cycle fatigue
    Yue, Peng
    Ma, Juan
    Huang, Han
    Shi, Yang
    Zu, Jean W.
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 150
  • [10] Fatigue Life Analysis Based on Transition State Parameters of Turbine Blades
    Chen, Yingtao
    Yang, Xinlong
    Ai, Yanting
    Guan, Peng
    Zhang, Wanlin
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2024, 24 (04) : 1889 - 1905
12345