Evolution mechanism of alumina coating layer on rutile TiO2 powders and the pigmentary properties

被引：46

作者：

Liu, Yumin ^{[1
]}

Zhang, Yunsheng ^{[1
]}

Ge, Chen ^{[1
]}

Yin, Hengbo ^{[1
]}

Wang, Aili ^{[1
]}

Ren, Min ^{[1
]}

Feng, Hui ^{[1
]}

Chen, Jun ^{[1
]}

Jiang, Tingshun ^{[1
]}

Yu, Longbao ^{[1
]}

机构：

[1] Jiangsu Univ, Fac Chem & Chem Engn, Zhenjiang 212013, Peoples R China

来源：

APPLIED SURFACE SCIENCE | 2009年 / 255卷 / 16期

关键词：

Rutile TiO2; Alumina; Coating layer; Coating; PARTICLES;

D O I：

10.1016/j.apsusc.2009.04.013

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The evolution of alumina coating layers on rutile TiO2 particle surfaces was investigated starting from aluminum sulfate by a chemical liquid deposition method. The morphology of the alumina coating layers was determined by transmission electron microscopy. The chemical structure and the evolution mechanism of the alumina coating layers on TiO2 surfaces were investigated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and powder X-ray diffraction techniques. The dispersibility of the alumina-coated TiO2 powders was determined by dynamic laser scattering (DLS) mode. The alumina coating layers existed in boehmite phase, AlOOH, and anchored at the surfaces of TiO2 via Ti-O-Al bond. The formation of alumina coating layers on TiO2 surfaces depended on the pH value of the deposition solution and the alumina loading. After coated by alumina layer, the dispersibility, whiteness, brightness, and light scattering index of the resultant samples were promoted. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：7427 / 7433

页数：7

共 9 条

[1] Sol-gel synthesized of nanocomposite palladium-alumina ceramic membrane for H2 permeability:: Preparation and characterization [J].

Ahmad, A. L. ;

Mustafa, N. N. N. .

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2007, 32 (12) :2010-2021

[2] Synthesis, characterization and performance of NiMo catalysts supported on titania modified alumina for the hydroprocessing of different gas oils derived from Athabasca bitumen [J].

Ferdous, D. ;

Bakhshi, N. N. ;

Dalai, A. K. ;

Adjaye, J. .

APPLIED CATALYSIS B-ENVIRONMENTAL, 2007, 72 (1-2) :118-128

[3] Characteristics and properties of surface coated nano-TiO2 [J].

Gao Jia-cheng ;

Zou Jian ;

Tan Xiao-wei ;

Wang Yong .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 (06) :1252-1258

[4] Surface characteristics of hydrous silica-coated TiO2 particles [J].

Lin, YL ;

Wang, TJ ;

Jin, Y .

POWDER TECHNOLOGY, 2002, 123 (2-3) :194-198

[5] Effects of coating parameters on the morphology of SiO2-coated TiO2 and the pigmentary properties [J].

Liu, Yumin ;

Ge, Chen ;

Ren, Min ;

Yin, Hengbo ;

Wang, Aili ;

Zhang, Dongzhi ;

Liu, Chunyan ;

Chen, Jun ;

Feng, Hui ;

Yao, Hengping ;

Jiang, Tingshun .

APPLIED SURFACE SCIENCE, 2008, 254 (09) :2809-2819

[6] Control of the photocatalytic activity of TiO2 nanoparticles by silica coating with polydiethoxysiloxane [J].

Siddiquey, Iqbal Ahmed ;

Furusawa, Takeshi ;

Sato, Masahide ;

Honda, Kozue ;

Suzuki, Noboru .

DYES AND PIGMENTS, 2008, 76 (03) :754-759

[7] Dispersion stability and photo-activity of rutile (TiO2) powders [J].

van Dyk, AC ;

Heyns, AM .

JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1998, 206 (02) :381-391

[8] Film-coating process of hydrated alumina on TiO2 particles [J].

Wu, HX ;

Wang, TJ ;

Jin, Y .

INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2006, 45 (04) :1337-1342

[9] A comparative study of the adsorption and desorption of o-xylene onto bentonite clay and alumina [J].

Zaitan, Hicham ;

Bianchi, Daniel ;

Achak, Ouafae ;

Chafik, Tarik .

JOURNAL OF HAZARDOUS MATERIALS, 2008, 153 (1-2) :852-859

← 1 →