Magnetic properties of ball-milled nanocrystalline alloys Fe78B13Si9

Magnetic properties of nanocrystalline Fe78B13Si9 alloys are studied for three series prepared by ball milling starting from amorphous ribbons, crystallized ribbons, and elemental powders. Temperature variation of static magnetization results in strong ferromagnetic interaction which is weakly dependent on the initial material. Magnetic hysteresis loops show that saturation magnetization, magnetic remanence, and coercive field increase with frequency for both series of ribbon samples, whereas they decrease for alloys prepared from elemental powders. Power losses raise faster for the alloys prepared from elemental powders than for the two other alloys.