Strain-rate effects on microstructural deformation in irradiated 316 SS

被引:4
作者
Cole, JI
Tsai, H
Allen, TR
Yoshitake, T
Akasaka, N
Yamagata, I
Nakamura, Y
机构
[1] Idaho Natl Lab, Nucl Fuels & Mat Dept, Idaho Falls, ID USA
[2] Argonne Natl Lab, Argonne, IL 60439 USA
[3] Univ Wisconsin, Madison, WI 53706 USA
[4] Japan Atom Energy Res & Dev Agcy, Oarai, Ibaraki, Japan
关键词
D O I
10.1016/j.jnucmat.2006.02.034
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A series of studies have been performed to investigate the post-irradiation deformation and failure behavior of 12% cold-worked 316 stainless steel following irradiation to variety of doses and temperatures in the outer rows of the experimental breeder reactor II (EBR-II). In the current phase of these studies, three sets of samples with different radiation-induced microstructures have been characterized with transmission electron microscopy (TEM) following tensile testing to failure at a 'fast' strain-rate (1 x 10(-3) s(-1)) and a 'slow' strain-rate (1 x 10(-7) s(-1)). The samples were irradiated to doses between 9 and 41 dpa at temperatures between 383 and 443 degrees C. Tensile tests were conducted at a temperature of 430 degrees C and only regions outside of the necked region were examined. Over the parameters tested, strain-rate had a negligible effect on the deformation microstructure. In addition, there was no clear evidence of localized deformation behavior and the deformation appeared relatively homogeneous, characterized by unfaulting and incorporation of faulted dislocation loops into the general dislocation network structure. The influence of the defect microstructures and strain-rate on deformation behavior is discussed. Published by Elsevier B.V.
引用
收藏
页码:316 / 323
页数:8
相关论文
共 14 条
[1]  
BRUEMMER SM, 1987, MRS S P MICR EV IRR, P437
[2]   Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels [J].
Byun, TS ;
Hashimoto, N ;
Farrell, K .
ACTA MATERIALIA, 2004, 52 (13) :3889-3899
[3]   Plastic instability in polycrystalline metals after low temperature irradiation [J].
Byun, TS ;
Farrell, K .
ACTA MATERIALIA, 2004, 52 (06) :1597-1608
[4]   Plastic deformation in 316LN stainless steel - characterization of deformation microstructures [J].
Byun, TS ;
Lee, EH ;
Hunn, JD .
JOURNAL OF NUCLEAR MATERIALS, 2003, 321 (01) :29-39
[5]   POSTIRRADIATION DEFORMATION CHARACTERISTICS OF HEAVY-ION IRRADIATED 304L SS [J].
COLE, JI ;
BRUEMMER, SM .
JOURNAL OF NUCLEAR MATERIALS, 1995, 225 :53-58
[6]  
COLE JI, 1995, P 7 INT S ENV DEGR M, P817
[7]  
HAMILTON ML, 1987, ASTM STP, V956, P245
[8]   Origin of hardening and deformation mechanisms in irradiated 316 LN austenitic stainless steel [J].
Lee, EH ;
Byun, TS ;
Hunn, JD ;
Farrell, K ;
Mansur, LK .
JOURNAL OF NUCLEAR MATERIALS, 2001, 296 :183-191
[9]   DISLOCATION CHANNELING IN NEUTRON-IRRADIATED MOLYBDENUM [J].
MASTEL, B ;
BIERLEIN, TK ;
KISSINGER, HE ;
LAIDLER, JJ .
JOURNAL OF APPLIED PHYSICS, 1963, 34 (12) :3637-&
[10]   INHOMOGENEOUS DEFORMATION-BEHAVIOR OF NEUTRON-IRRADIATED ZIRCALOY-2 [J].
ONCHI, T ;
KAYANO, H ;
HIGASHIGUCHI, Y .
JOURNAL OF NUCLEAR MATERIALS, 1980, 88 (2-3) :226-235