Mathematical Model for Prediction of Composition of Inclusions Formed during Solidification of Liquid Steel

被引:178
作者
Choudhary, S. K. [1 ]
Ghosh, A. [1 ]
机构
[1] Tata Steel, Div Res & Dev, Jamshedpur 831001, Bihar, India
关键词
steelmaking; continuous casting; steel billets; solidification; segregation models; inclusions; SOLUTE REDISTRIBUTION; OXIDE-INCLUSIONS; MNS PRECIPITATION; CALCIUM-TREATMENT; DEOXIDATION; MICROSEGREGATION; DIFFUSION;
D O I
10.2355/isijinternational.49.1819
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Non-metallic inclusions originate mainly during secondary steelmaking due to deoxidation and other exogenous sources. Additional inclusions form during cooling and subsequent freezing of liquid steel. Rejection of solutes by the solidifying dendrites causes segregation of solutes in the interdendritic liquid with consequent build-up of their thermodynamic supersaturation. The work reported in the present paper was undertaken to develop a computation procedure for prediction of inclusion compositions formed during cooling and solidification of liquid steel. The model has been applied to an inclusion sensitive grade of steel. Segregation of various solutes with progress of freezing has been calculated using the Clyne-Kurz microsegregation equation. A sequential computation procedure involving segregation equation and thermodynamic equilibrium calculations by the Factsage thermodynamic software has been developed. Compositions of inclusions at various solid fractions have been determined. Model predictions have been compared with literature as well as with inclusion compositions determined in continuously cast billet samples using SEM-EDS. Reasonably good correspondence between model predictions and observed inclusions have been obtained.
引用
收藏
页码:1819 / 1827
页数:9
相关论文
共 31 条
[1]   FactSage thermochemical software and databases [J].
Bale, C ;
Chartrand, P ;
Degterov, SA ;
Eriksson, G ;
Hack, K ;
Ben Mahfoud, R ;
Melançon, J ;
Pelton, AD ;
Petersen, S .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2002, 26 (02) :189-228
[2]  
BRODY HD, 1966, T METALL SOC AIME, V236, P615
[3]   SOLUTE REDISTRIBUTION DURING SOLIDIFICATION WITH RAPID SOLID-STATE DIFFUSION [J].
CLYNE, TW ;
KURZ, W .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (06) :965-971
[4]   Modelling of manganese sulphide formation during solidification, part I: Description of MnS formation parameters [J].
Diederichs, R ;
Bleck, W .
STEEL RESEARCH INTERNATIONAL, 2006, 77 (03) :202-209
[5]  
Fauling G.M., 1999, IRON STEELMAKER, V26, P29
[6]  
Gaye H, 1998, ALEX MCLEAN SYMPOSIUM PROCEEDINGS, P67
[7]   Thermodynamic examination of inclusion modification and precipitation from calcium treatment to solidified steel [J].
Holappa, L ;
Hämäläinen, M ;
Liukkonen, M ;
Lind, M .
IRONMAKING & STEELMAKING, 2003, 30 (02) :111-115
[8]   INFLUENCE OF CALCIUM-TREATMENT ON SULFIDE-INCLUSIONS AND OXIDE-INCLUSIONS IN CONTINUOUS-CAST SLAB OF CLEAN STEEL - DENDRITE STRUCTURE AND INCLUSIONS [J].
IMAGUMBAI, M ;
TAKEDA, T .
ISIJ INTERNATIONAL, 1994, 34 (07) :574-583
[9]   DENDRITE MORPHOLOGY OF STEADY-STATE UNIDIRECTIONALLY SOLIDIFIED STEEL [J].
JACOBI, H ;
SCHWERDTFEGER, K .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (06) :811-820
[10]   A thermodynamic model for deoxidation equilibria in steel [J].
Jung, IH ;
Decterov, SA ;
Pelton, AD .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2004, 35 (03) :493-507