The influence of the heat treatment temperature in the magnetic characteristics of a SiO2-Li2O-Fe2O3 glass prepared by sol-gel

被引：2
作者：
Graca, M. P. F. [1 ]
Lopes, J. C. [1 ,2 ]
Costa, B. F. O. [3 ]
Mendiratta, S. K. [1 ]
Valente, M. A. [1 ]
机构：
[1] Univ Aveiro, Dept Phys, Aveiro I3N, P-3810193 Aveiro, Portugal
[2] Univ Algarve, Fac Sci & Technol, Dept Phys, P-8000117 Faro, Portugal
[3] Univ Coimbra, Dept Phys, CEMDRX, P-3004516 Coimbra, Portugal
来源：
JOURNAL OF NON-CRYSTALLINE SOLIDS | 2014年 / 391卷
关键词：
Glasses; Sol-gel; Structural properties; Magnetic properties; LITHIUM FERRITE NANOPARTICLES; IRON;
D O I：
10.1016/j.jnoncrysol.2014.03.008
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The glass with the molar composition 88SiO(2)-2Li(2)O-10Fe(2)O(3) (mole %) was prepared by the sol-gel route and after heat-treated at temperatures between 250 and 1000 degrees C under oxidizing conditions. Crystalline phases (LiFe5O8, SiO2, Fe2O3 and LiFe(Si2O6)) were observed by X-ray powder diffraction in the glasses treated at temperatures above 800 degrees C. Scanning electron micrographs reveal the presence of particles in the samples heat-treated up to 800 degrees C, which are essentially amorphous or with an incipient crystallization. The increase of the heat-treatment temperature promotes the coarsening of particles. The magnetic characteristics of the prepared glasses and glass ceramics were performed using a vibrating sample magnetometer in function of the magnetic field amplitude (-10 T <= B <= 10 T) and in function of temperature (5 K-300 K). The samples heat-treated at 900 and 1000 degrees C present a ferrimagnetic behavior accompanied by the appearance of peaks corresponding to the lithium ferrite phase (LiFe5O8). A curious aspect is the saturation magnetization of the sample heat-treated at 800 degrees C is the highest of all samples, indicating the highest amount of LiFe5O8 crystals. The Mossbauer results are in accordance with the magnetization and magnetic susceptibility measurements. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：32 / 38
页数：7
相关论文
共 23 条
  • [1] Low temperature preparation of β-LiFe5O8 fine particles by hydrothermal ball milling
    Ahniyaz, A
    Fujiwara, T
    Song, SW
    Yoshimura, M
    [J]. SOLID STATE IONICS, 2002, 151 (1-4) : 419 - 423
  • [2] An Sung Yong, 2005, J MAGN MAGN MATER, V290-291, P1551
  • [3] Blackburn W. D. S., 2006, MAGNETIC PROPERTIES
  • [4] Crystallization and properties of sol-gel derived 10Fe2O3-10Al2O3-80SiO2 glass-ceramics
    da Silva, MGF
    Valente, MA
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1998, 232 : 409 - 415
  • [5] The iron behaviour in aluminosilicate gel-derived materials
    Da Silva, MGF
    Valente, MA
    [J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2000, 17 (01) : 47 - 53
  • [6] Infrared and Mossbauer studies of iron in aluminosilicate glasses
    da Silva, MGF
    Costa, BFO
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 2001, 293 : 534 - 538
  • [7] Spectroscopy studies of NiFe2O4 nanosized powders obtained using coconut water
    de Paiva, J. A. C.
    Graca, M. P. F.
    Monteiro, J.
    Macedo, M. A.
    Valente, M. A.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 485 (1-2) : 637 - 641
  • [8] Phase investigation of as-prepared iron oxide/hydroxide produced by sol-gel synthesis
    Duraes, L
    Costa, BFO
    Vasques, J
    Campos, J
    Portugal, A
    [J]. MATERIALS LETTERS, 2005, 59 (07) : 859 - 863
  • [9] Preparation, structure, morphology, and dc and ac conductivity of the 88SiO2-6Li2O-6Nb2O5 (% mole) sol-gel derived glass-ceramics
    Graca, M. P. F.
    Ferreira da Silva, M. G.
    Valente, M. A.
    [J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2007, 42 (01) : 1 - 8
  • [10] Magnetic Properties of Lithium Ferrite Nanoparticles with a Core/Shell Structure
    Jovic, Natasa
    Antic, Bratislav
    Goya, Gerardo F.
    Spasojevic, Vojislav
    [J]. CURRENT NANOSCIENCE, 2012, 8 (05) : 651 - 658
123