Stress intensity factors for surface cracks at countersunk holes

被引：12
作者：
Park, Chul Young
Grandt, Alten F., Jr.
Suh, Jung Jun
机构：
[1] Eclipse Aviat Corp, Albuquerque, NM 87106 USA
[2] Purdue Univ, Sch Aeronaut & Astronaut, W Lafayette, IN 47907 USA
来源：
ENGINEERING FRACTURE MECHANICS | 2006年 / 73卷 / 13期
关键词：
stress intensity factor; countersunk hole; crack closure; PMMA;
D O I：
10.1016/j.engfracmech.2006.02.017
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Fatigue crack growth from countersunk fastener holes loaded in remote tensile loading was studied using the transparent polymer PMMA. A single edge corner crack at the bottom of the plate and a single internal surface crack at the sharp intersection between the bore and the countersink were induced in the PMMA specimens by pre-cracking. The specimens were then fatigue tested under constant amplitude remote tensile loading and the 'back-calculation' method was used to determine stress intensity factors at several crack front locations. When variations in fatigue crack closure were taken into account, the experimental stress intensity factors agreed well with the computational results at selected crack fronts. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1878 / 1898
页数：21
相关论文
共 50 条
[41]   Finite element based evaluation of stress intensity factors for interactive semi-elliptic surface cracks [J].
Sethuraman, R ;
Reddy, GSS ;
Ilango, IT .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2003, 80 (12) :843-859
[42]   Two-dimensional weight function of stress intensity factors for external circumferential surface cracks in cylinders [J].
Yuan, Kuilin ;
Dong, Kun ;
Li, Linyue .
Hanjie Xuebao/Transactions of the China Welding Institution, 2025, 46 (04) :61-71
[43]   Evaluating stress intensity factors for surface cracks in an orthotropic steel deck accounting for the welding residual stresses [J].
Qiang, Bin ;
Wang, Xin .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 110
[44]   General point load weight function of stress intensity factors for external circumferential surface cracks in pipes [J].
Yuan, Kuilin ;
Dong, Kun ;
Fang, Qitian .
OCEAN ENGINEERING, 2024, 308
[45]   Stress intensity factors for high aspect ratio semi-elliptical internal surface cracks in pipes [J].
Li, C. Q. ;
Yang, S. T. .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2012, 96-97 :13-23
[46]   Weight function and stress intensity factors for external circumferential surface cracks with high aspect ratio in cylinders [J].
Yuan, Kuilin ;
Dong, Kun ;
Fang, Qitian ;
Zhen, Chunbo .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2024, 212
[47]   Round Robin Analyses on Stress Intensity Factors of Inner Surface Cracks in Welded Stainless Steel Pipes [J].
Han, Chang-Gi ;
Chang, Yoon-Suk ;
Kim, Jong-Sung ;
Kim, Maan-Won .
NUCLEAR ENGINEERING AND TECHNOLOGY, 2016, 48 (06) :1412-1422
[48]   Three-dimensional weight function analyses and stress intensity factors for two eccentric and asymmetric surface cracks and surface-corner cracks at a circular hole [J].
Xu, Wu ;
Zhang, Bo ;
Wu, Xue-Ren .
ENGINEERING FRACTURE MECHANICS, 2023, 277
[49]   Stress intensity factors for embedded elliptical cracks in cylindrical and spherical vessels [J].
Livieri, Paolo ;
Segala, Fausto .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2016, 86 :260-266
[50]   Stress intensity factors for circumferential cracks in pressure vessel door closures [J].
Casey, GA ;
Hyde, TH ;
Warrior, NA ;
Smith, B .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1999, 76 (01) :1-12
12345