Stress intensity factors for surface cracks at countersunk holes

被引：12
作者：
Park, Chul Young
Grandt, Alten F., Jr.
Suh, Jung Jun
机构：
[1] Eclipse Aviat Corp, Albuquerque, NM 87106 USA
[2] Purdue Univ, Sch Aeronaut & Astronaut, W Lafayette, IN 47907 USA
来源：
ENGINEERING FRACTURE MECHANICS | 2006年 / 73卷 / 13期
关键词：
stress intensity factor; countersunk hole; crack closure; PMMA;
D O I：
10.1016/j.engfracmech.2006.02.017
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Fatigue crack growth from countersunk fastener holes loaded in remote tensile loading was studied using the transparent polymer PMMA. A single edge corner crack at the bottom of the plate and a single internal surface crack at the sharp intersection between the bore and the countersink were induced in the PMMA specimens by pre-cracking. The specimens were then fatigue tested under constant amplitude remote tensile loading and the 'back-calculation' method was used to determine stress intensity factors at several crack front locations. When variations in fatigue crack closure were taken into account, the experimental stress intensity factors agreed well with the computational results at selected crack fronts. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1878 / 1898
页数：21
相关论文
共 50 条
[31]   Calculation of stress intensity factors for interlaminar cracks in composite laminates [J].
Qian, W ;
Sun, CT .
COMPOSITES SCIENCE AND TECHNOLOGY, 1997, 57 (06) :637-650
[32]   Stress intensity factors and initiation of unequal collinear cracks in rock [J].
Xi, Jing-Yi ;
Chen, Zhong-Hui ;
Zhu, Di-Jie ;
Chen, Qing-Feng .
Yantu Gongcheng Xuebao/Chinese Journal of Geotechnical Engineering, 2015, 37 (04) :727-733
[33]   On estimating stress intensity factors and modulus of cohesion for fractal cracks [J].
Wnuk, MP ;
Yavari, A .
ENGINEERING FRACTURE MECHANICS, 2003, 70 (13) :1659-1674
[34]   Stress intensity factors for two periodical rows of collinear cracks [J].
Galybin, AN .
ENGINEERING FRACTURE MECHANICS, 1998, 59 (03) :281-288
[35]   A pratical method of stress intensity factors for two collinear cracks [J].
Chen J. ;
Fan X. ;
Huang Y. .
Huazhong Keji Daxue Xuebao (Ziran Kexue Ban)/Journal of Huazhong University of Science and Technology (Natural Science Edition), 2017, 45 (04) :61-67
[36]   A unified definition for stress intensity factors of interface corners and cracks [J].
Hwu, Chyanbin ;
Kuo, T. L. .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2007, 44 (18-19) :6340-6359
[37]   Mixed‐Mode Stress Intensity Factors for Partially Opened Cracks [J].
Theo Fett .
International Journal of Fracture, 2001, 111 (4) :0-0
[38]   Approximate Determination of Stress Intensity Factor for Multiple Surface Cracks [J].
Kastratovic, Gordana ;
Vidanovic, Nenad ;
Grbovic, Aleksandar ;
Rasuo, Bosko .
FME TRANSACTIONS, 2018, 46 (01) :39-45
[39]   Three-dimensional weight function analyses and stress intensity factors for two unsymmetric surface cracks and surface-corner cracks at a circular hole [J].
Zhang, Bo ;
Xu, Wu ;
Wu, Xue-Ren .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2022, 122
[40]   Stress intensity factor correction for asymmetric through-thickness fatigue cracks at holes [J].
Stefanescu, D ;
Edwards, L ;
Fitzpatrick, ME .
INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (07) :569-576
12345