Stress intensity factors for surface cracks at countersunk holes

被引：12
作者：
Park, Chul Young
Grandt, Alten F., Jr.
Suh, Jung Jun
机构：
[1] Eclipse Aviat Corp, Albuquerque, NM 87106 USA
[2] Purdue Univ, Sch Aeronaut & Astronaut, W Lafayette, IN 47907 USA
来源：
ENGINEERING FRACTURE MECHANICS | 2006年 / 73卷 / 13期
关键词：
stress intensity factor; countersunk hole; crack closure; PMMA;
D O I：
10.1016/j.engfracmech.2006.02.017
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Fatigue crack growth from countersunk fastener holes loaded in remote tensile loading was studied using the transparent polymer PMMA. A single edge corner crack at the bottom of the plate and a single internal surface crack at the sharp intersection between the bore and the countersink were induced in the PMMA specimens by pre-cracking. The specimens were then fatigue tested under constant amplitude remote tensile loading and the 'back-calculation' method was used to determine stress intensity factors at several crack front locations. When variations in fatigue crack closure were taken into account, the experimental stress intensity factors agreed well with the computational results at selected crack fronts. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1878 / 1898
页数：21
相关论文
共 50 条
  • [21] Stress intensity factors for branching cracks in space structures
    Zvyagin, A., V
    Luzhin, A. A.
    Smirnov, N. N.
    Shamina, A. A.
    Shamin, A. Y.
    ACTA ASTRONAUTICA, 2021, 180 : 66 - 72
  • [22] Stress intensity factors of elliptical cracks at the weld toe
    Livieri, Paolo
    Segala, Fausto
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2023, 128
  • [23] A numerical analysis of stress intensity factors at bifurcated cracks
    Yan, XQ
    ENGINEERING FAILURE ANALYSIS, 2006, 13 (04) : 629 - 637
  • [24] Stress concentration factor analysis of countersunk holes using finite element analysis and response surface methodology
    Gharaibeh, Mohammad A.
    Tlilan, Hitham
    Gharaibeh, Belal M. Y.
    AUSTRALIAN JOURNAL OF MECHANICAL ENGINEERING, 2021, 19 (01) : 30 - 38
  • [25] Cracks at elliptical holes: Stress intensity factor and Finite Fracture Mechanics solution
    Weissgraeber, P.
    Felger, J.
    Geipel, D.
    Becker, W.
    EUROPEAN JOURNAL OF MECHANICS A-SOLIDS, 2016, 55 : 192 - 198
  • [26] Stress intensity factors and crack interaction in adjacent holes
    de Rijck, JJM
    Fawaz, SA
    ENGINEERING FRACTURE MECHANICS, 2001, 68 (07) : 963 - 969
  • [27] On the calculation of stress intensity factors for surface cracks in welded pipe-plate and tubular joints
    Wang, X
    Lambert, SB
    INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (01) : 89 - 96
  • [28] Stress intensity factors of through-thickness and surface cracks in tubular Y-joints
    Chiew, SP
    Lie, ST
    Lee, CK
    Huang, ZW
    PROCEEDINGS OF THE ELEVENTH (2001) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL IV, 2001, : 30 - 36
  • [29] Stress intensity factors for semi-elliptical surface cracks in semicircularly notched tension plates
    Lin, XB
    Smith, RA
    JOURNAL OF STRAIN ANALYSIS FOR ENGINEERING DESIGN, 1997, 32 (03) : 229 - 236
  • [30] The Evolution of Stress Intensity Factors and the Propagation of Cracks in Elastic Media
    Avner Friedman
    Bei Hu
    Juan J. L. Velazquez
    Archive for Rational Mechanics and Analysis, 2000, 152 : 103 - 139
12345