Stress intensity factors for surface cracks at countersunk holes

被引：12
作者：
Park, Chul Young
Grandt, Alten F., Jr.
Suh, Jung Jun
机构：
[1] Eclipse Aviat Corp, Albuquerque, NM 87106 USA
[2] Purdue Univ, Sch Aeronaut & Astronaut, W Lafayette, IN 47907 USA
来源：
ENGINEERING FRACTURE MECHANICS | 2006年 / 73卷 / 13期
关键词：
stress intensity factor; countersunk hole; crack closure; PMMA;
D O I：
10.1016/j.engfracmech.2006.02.017
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Fatigue crack growth from countersunk fastener holes loaded in remote tensile loading was studied using the transparent polymer PMMA. A single edge corner crack at the bottom of the plate and a single internal surface crack at the sharp intersection between the bore and the countersink were induced in the PMMA specimens by pre-cracking. The specimens were then fatigue tested under constant amplitude remote tensile loading and the 'back-calculation' method was used to determine stress intensity factors at several crack front locations. When variations in fatigue crack closure were taken into account, the experimental stress intensity factors agreed well with the computational results at selected crack fronts. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1878 / 1898
页数：21
相关论文
共 50 条
[1]   Stress intensity factors for corner cracks emanating from fastener holes under tension [J].
Lin, XB ;
Smith, RA .
ENGINEERING FRACTURE MECHANICS, 1999, 62 (06) :535-553
[2]   Estimation of stress intensity factors for semi-elliptical surface cracks [J].
Fett, T .
ENGINEERING FRACTURE MECHANICS, 2000, 66 (04) :349-356
[3]   Stress intensity factors of two close surface cracks and their interaction criterion [J].
Sumitomo Metal Industries, Ltd., 1 8 Fuso cho, Amagasaki shi, Hyogo, 660-0891, Japan .
Nihon Kikai Gakkai Ronbunshu A, 2006, 9 (1310-1317) :1310-1317
[4]   Weight functions and stress intensity factors for quarter-elliptical corner cracks in fastener holes [J].
Chen, Q ;
Wang, X .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (08) :701-712
[5]   Stress intensity factors for part-elliptical cracks emanating from dimpled rivet holes [J].
Wang, Ailun ;
She, Chongmin ;
Lin, Gang ;
Zhou, You ;
Guo, Wanlin .
INTERNATIONAL JOURNAL OF COMPUTATIONAL MATERIALS SCIENCE AND ENGINEERING, 2014, 3 (04)
[6]   Development of Stress Intensity Factors for Surface Cracks With Large Aspect Ratio in Plates [J].
Li, Yinsheng ;
Hasegawa, Kunio ;
Katsumata, Genshichiro ;
Osakabe, Kazuya ;
Okada, Hiroshi .
JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2015, 137 (05)
[7]   Stress intensity factors and equations for tangential surface cracks in rotating hollow disks [J].
Ayhan, Ali O. .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 108
[8]   Empirical Stress Intensity Factors for Surface Cracks under Rolling Contact Fatigue [J].
Levesque, George ;
Arakere, Nagaraj K. .
TRIBOLOGY TRANSACTIONS, 2010, 53 (04) :621-629
[9]   Solutions of stress intensity factors of subsurface cracks [J].
Feng, X-Q. ;
Xu, M. .
FRACTURE OF MATERIALS: MOVING FORWARDS, 2006, 312 :83-88
[10]   ANALYSIS OF STRESS INTENSITY FACTORS FOR CURVED CRACKS [J].
NODA, NA ;
ODA, K ;
ISHII, K .
JSME INTERNATIONAL JOURNAL SERIES A-MECHANICS AND MATERIAL ENGINEERING, 1994, 37 (04) :360-365
12345