Effect of Impurities on the Phase Composition and Properties of a New Alloy of the Al-Y-Er-Zr-Sc System

被引:20
作者
Pozdnyakov, A. V. [1 ]
Barkov, R. Yu. [1 ]
机构
[1] Natl Res Technol Inst MISiS, Moscow, Russia
基金
俄罗斯科学基金会;
关键词
aluminum alloys; rare earth metals microstructure; heat treatment; hardness; MECHANICAL-PROPERTIES; RECRYSTALLIZATION BEHAVIOR; SI; MICROSTRUCTURE; EVOLUTION; RESISTANCE; ADDITIONS;
D O I
10.1007/s11015-019-00796-w
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
A comparative study is provided for the effect of Si and Fe impurities in relation to their concentration in the structure, phase composition, and mechanical properties of alloy Al-0.2Y-0.3Er-0.2Zr-0.05Sc. With a content of Fe and Si (in the amount of 0.15%), presence is noted of phases formed by iron and silicon impurities with an increased concentration of Zr, Er, and Y. These phases are not found in the structure of alloy with a lower concentration of Fe and Si (0.01%). Due to dilution of aluminum solid solution with Zr, Er and Y, alloy with an increased Fe and Si (0.15%) content shows a weaker hardening effect during annealing compared to alloy having a more supersaturated solid solution. Sc in both alloys is evenly distributed within the matrix of aluminum solid solution and does not form phases during crystallization. It is shown that the temperature for the start of recrystallization for these alloys is in the range 500-550 degrees C. The set of standard mechanical properties for sheet produced from these alloys is almost at the same level: yield strength of 155 MPa, ultimate strength of 166 MPa, elongation at 11.2% for alloy with 0.15% (Fe and Si) and 8.7% for alloy with 0.01% (Fe and Si). It is noted that after annealing (200 degrees C, 1 h) sheets hardness increases by 5 HV, which may point to aluminum solid solution decomposition.
引用
收藏
页码:79 / 86
页数:8
相关论文
共 25 条
[1]   Effect of Y on microstructure and mechanical properties of Al-Mg-Mn-Zr-Sc alloy with low Sc content [J].
Barkov, R. Yu. ;
Pozdniakov, A. V. ;
Tkachuk, E. ;
Zolotorevskiy, V. S. .
MATERIALS LETTERS, 2018, 217 :135-138
[2]   Synthesis of Aluminum-Based Scandium-Yttrium Master Alloys [J].
Bazhin, V. Yu. ;
Kosov, Ya. I. ;
Lobacheva, O. L. ;
Dzhevaga, N. V. .
RUSSIAN METALLURGY, 2015, 2015 (07) :516-520
[3]   Effect of Er additions on ambient and high-temperature strength of precipitation-strengthened Al-Zr-Sc-Si alloys [J].
Booth-Morrison, Christopher ;
Seidman, David N. ;
Dunand, David C. .
ACTA MATERIALIA, 2012, 60 (08) :3643-3654
[4]   Coarsening resistance at 400 °C of precipitation-strengthened Al-Zr-Sc-Er alloys [J].
Booth-Morrison, Christopher ;
Dunand, David C. ;
Seidman, David N. .
ACTA MATERIALIA, 2011, 59 (18) :7029-7042
[5]   Quasi-superplasticity of a banded-grained Al-Mg-Y alloy processed by continuous casting-extrusion [J].
Cao, Furong ;
Zhu, Xiaotong ;
Wang, Shuncheng ;
Shi, Lu ;
Xu, Guangming ;
Wen, Jinglin .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 690 :433-445
[6]   Effects of Er/Sr/Cu additions on the microstructure and mechanical properties of Al-Mg alloy during hot extrusion [J].
Che, Hongmei ;
Jiang, Xianquan ;
Qiao, Nan ;
Liu, Xiaokui .
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 708 :662-670
[7]   Mechanical properties and optimization of the aging of a dilute Al-Sc-Er-Zr-Si alloy with a high Zr/Sc ratio [J].
De Luca, Anthony ;
Dunand, David C. ;
Seidman, David N. .
ACTA MATERIALIA, 2016, 119 :35-42
[8]   Aging and recrystallization behavior of precipitation strengthened Al-0.25Zr-0.03Y alloy [J].
Gao, Haiyan ;
Feng, Wuqiang ;
Gu, Jing ;
Wang, Jun ;
Sun, Baode .
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 696 :1039-1045
[9]   Structural and compositional evolution of Al3(Zr,Y) precipitates in Al-Zr-Y alloy [J].
Gao, Haiyan ;
Feng, Wuqiang ;
Wang, Yufei ;
Gu, Jing ;
Zhang, Yongzhi ;
Wang, Jun ;
Sun, Baode .
MATERIALS CHARACTERIZATION, 2016, 121 :195-198
[10]   Microstructure and mechanical properties of Al-Mg-Er sheets jointed by friction stir welding [J].
Hao, H. L. ;
Ni, D. R. ;
Zhang, Z. ;
Wang, D. ;
Xiao, B. L. ;
Ma, Z. Y. .
MATERIALS & DESIGN, 2013, 52 :706-712