Synthesis and characterization of thermoresponsive N-isopropylacrylamide/methacrylated pullulan hydrogels

被引：27

作者：

Masci, G ^{[1
]}

Bontempo, D ^{[1
]}

Crescenzi, V ^{[1
]}

机构：

[1] Univ Roma La Sapienza, Dept Chem, I-00185 Rome, Italy

来源：

POLYMER | 2002年 / 43卷 / 20期

关键词：

temperature-responsive; poly(N-isopropylacrylamide); methacrylated pullulan;

D O I：

10.1016/S0032-3861(02)00415-9

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Thermosensitive hydrogels were prepared by free radical polymerization starting from a methacrylated pullulan derivative (acting as the cross-linker) and using N-isopropylacrylamide (NIPAAM) as the monomer. Several hydrogels were obtained by changing the monomer to cross-linker ratio. A significant thermosensitivity was observed only when the molar amount of NIPAAM incorporated in the network was at least eight times higher that of methacrylate groups on pullulan. The hydrogel with high amount of NIPAAM deswells more than 80% after the T-jump. The lower critical solution temperature of thermosensitive hydrogels decreases with increasing amount of NIPAAM. The mechanical properties of the hydrogels are strongly affected by the percentage of incorporated NIPAAM and by the temperature. (C) 2002 Published by Elsevier Science Ltd.

引用

页码：5587 / 5593

页数：7

共 35 条

[1]

[Anonymous], SCI AM

[2]

[Anonymous], 2004, J CONTROL RELEASE, DOI DOI 10.1016/j.jconrel.2003.12.025

[3]

[Anonymous], BIODEGRADABLE HYDROG

[4] Synthesis and characterization of acrylic acid-containing dextran hydrogels [J].