Rapid sintering of nanocrystalline 8 mol.%Y2O3-stabilized ZrO2 by high-frequency induction heating method

被引：43

作者：

Kim, Hwan-Cheol ^{[1
]}

Shon, In-Jin ^{[1
]}

Jeong, In-Kyoon ^{[1
]}

Ko, In-Yong ^{[1
]}

机构：

[1] Chonbuk Natl Univ, Dept Adv Mat Engn, Res Ctr Adv Mat Dev, Engn Res Inst, Jeonbuk 560756, South Korea

来源：

METALS AND MATERIALS INTERNATIONAL | 2006年 / 12卷 / 05期

关键词：

sintering; mechanical properties; microstructure; nanomaterials; hardness;

D O I：

10.1007/BF03027705

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Using a high-frequency induction-heating sintering (HFIHS) method, nanocrystalline 8 mol.%Y2O3-stabilized ZrO2 was obtained from ultra fine powders. The observed advantages of this process include very quick densification to near theoretical density and prohibition of grain growth in namo-structured materials. Nearly fully dense nanocrystalline 8 mol%Y2O3-stabilized ZrO2, with a relative density of up to 99.8%, could be obtained with simultaneous application of 100 MPa pressure and an induced current within 10 min of sintering time without significant change in grain size. The influences of the sintering temperature and the mechanical pressure on the final density and grain size, of the products were investigated. The hardness and fracture toughness of the dense ZrO2 ceramics produced by HFIHS were investigated.

引用

页码：393 / 398

页数：6

共 50 条

[1] Rapid sintering of nanocrystalline 8 mol.%Y2O3-stabilized ZrO2 by high-frequency induction heating method [J].

Hwan -Cheol Kim ;

In -Jin Shon ;

In -Kyoon Jeong ;

In -Yong Ko .

Metals and Materials International, 2006, 12 :393-398

[2] Cold sintering process for 8 mol%Y2O3-stabilized ZrO2 ceramics [J].

Guo, Hanzheng ;

Bayer, Thorsten J. M. ;

Guo, Jing ;

Baker, Amanda ;

Randall, Clive A. .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (05) :2303-2308

[3] Sintering behavior of ultra-fine Al2O3-(ZrO2 + X mol% Y2O3) ceramics by high-frequency induction heating [J].

Kim, S. W. ;

Cockcroft, S. L. ;

Khalil, K. A. ;

Ogi, K. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (18-19) :4926-4931

[4] Densification Kinetics of CeO2 Reinforced 8 Mol.% Y2O3 Stabilized ZrO2 Ceramics [J].

Gupta, Alka ;

Nisar, Ambreen ;

Omar, Shobit ;

Balani, Kantesh .

JOM, 2018, 70 (10) :1937-1945

[5] Controllable preparation of 5mol% Y2O3-stabilized tetragonal ZrO2 by hydrothermal method [J].

Song, Jianhui ;

Zhang, He ;

Feng, Zongyu ;

Zhang, Jianxing ;

Chen, Fang ;

Long, Zhiqi ;

Huang, Xiaowei .

JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 856 (856)

[6] High-temperature deformation behaviour of TiO2-doped 2 mol.% Y2O3-stabilized ZrO2 (8Y-CSZ) under tension and compression [J].

Tekeli, Suleyman ;

Chen, Tiandan ;

Nagayama, Hitoshi ;

Sakuma, Taketo ;

Mecartney, Martha L. .

CERAMICS INTERNATIONAL, 2007, 33 (05) :869-874

[7] High-frequency induction heating sintering of ultra-fine Al2O3-(ZrO2+X%mol Y2O3) bioceramics [J].

Kim, S. W. ;

Khalil, K. A. ;

Ogi, K. .

ADVANCED MATERIALS AND PROCESSING IV, 2007, 29-30 :235-+

[8] Sintering of Y2O3-Stabilized ZrO2 Powders Obtained by Different Chemical Methods [J].

Salem, R. E. P. ;

Chinelatto, A. L. ;

Chinelatto, A. S. A. .

ADVANCED POWDER TECHNOLOGY VI, 2008, 591-593 :649-653

[9] Effect of N2 sintering atmosphere on the hardness of sol-gel films of 3 mol% Y2O3-stabilized ZrO2 [J].

Diaz-Parralejo, A. ;

Ortiz, A. L. ;

Rodriguez-Rojas, F. ;

Guiberteau, F. .

THIN SOLID FILMS, 2010, 518 (10) :2779-2782

[10] Rapid sintering of Al2O3-8YSZ bioceramic composites by high-frequency induction heating [J].

Khalil, KA ;

Dewidar, MM ;

Kyoon, JI ;

Kim, SW .

MULTISCALE DAMAGE RELATED TO ENVIRONMENT ASSISTED CRACKING, 2005, :137-143

← 1 2 3 4 5 →